The effects of dioctylphthalate (DOP), a plasticizer, and Acryloid K-125, a processing aid, on the rheological and physical properties of polyvinylchloride (PVC) were investigated. DOP reduced viscosity and the first mormal stress difference, while Acryloid K-125 noticeably increased them. Both DOP and Acryloid K-125, however, decreased the flow activation energy. Further, the flow activation energy was decreased with increasing shear rate. Over the DOP content tested, DOP reduced glass transition temperature, yield strain, and elongation to break. But incorporation of DOP up to 6 phi slightly increased the tensile strength and the tensile modulus. Investigation of microstructure of tensile fractured surface revealed that DOP makes PVC more brittle. Judging from density variations, DOP seemed to play a role in enhancing the chain orderness of PVC.

가소제로 사용되는 DOP와 가공조제로 사용되는 Acryloid K-125가 PVC의 유성학적성질 및 물성에 미치는 영향을 고찰하였다. 점도와 제1법선 응력차는 DOP의 첨가량이 증가함에 따라 감소하였으나 Acryloid K-125를 첨가한 경우에는 증가하였다. DOP와 Acryloid K-125는 모두 PVC의 유동활성화에너지를 감소시켰으며, 전단속도가 증가함에 따라 유동활성화에너지는 감소하였다. DOP를 첨가한 경우 유리전이온도, 항복응력 및 절단 신도는 감소하였다. 그러나, DOP의 함유량이 6 phr까지는 인장강도와 인장탄성율이 오히려 증가하는 경향을 나타내었다. 인장절단시편의 표면미세구조를 보면 DOP의 첨가가 PVC를 brittle하게 변화시킴을 알 수 있다. 밀도의 변화를 관찰한 결과 이 현상은 PVC 분자쇄의 치밀한 배열에 기인한 것이라 사료된다.