The permeation experiments of polyetherurethane membranes were studied by using 7 different alcohols in aqueous solution. The results indicated that water flux, J_w (mol/cm²·sec) and hydraulic permeability coefficient, K_w (mol/cm·sec·atm) wire increased with temperature, pressure and molecular weight of polyethylene glycol. Separation of solute alcohol were decreased with increasing the Taft number, σ^*, acidity, Δν_s cm^-2, and steric parameter, E^s of alcohol, in the order, t-butanol> sec-butanol> iso-butanol> iso-propanol> n-butanol> n-propanol> ethanol. It was also shown that the relative hydrogen-banding ability of the solute affected the preferential sorption of solute at the membrane surface. The effect of non-polar parameter, _s(H₂0) on alcohol separations increased with increasing molecular weight of alcohol and decreased in the order t-> sec-> iso-> n-, when the molecular weight was same.

폴리우레탄막의 액체투과특성을 검토하기 위하여 메틸렌비스(4-페닐이소시아네이트)와 평균분자량이 다른 폴리에틸렌글리콜을 용액중합하여 폴리에테르형 우레탄막을 제조하였으며 투과물질로는 특성이 서로 다른 7종의 알코올을 사용하였다. 투과실험결과로부터 폴리우레탄막을 통한 물의 투과는 투과압력 및 투과온도가 상승함에 따라 Water flux, J_w(mole/㎠·sec) 및 투과계수 K_w (mol/cm.sec.atm)는 증가되었으며 폴리에틸렌글리콜의 분자량이 커짐에 따라 J_w 및 K_w도 증가되었다. 또한 수용성알코올용액의 용질분산율, f(%)는 알코올의 Taft number, σ^*, 산성도, Δν_s cm^-2 및 입체인자, E_s가 커짐에 따라 t-부탄올>sec>-부탄올>i-부탄올>i-프로판올>n-부탄올>n-프로판올>에탄올순으로 감소되었다. 막의 우레탄기 및 에테르기와 알코올간의 수소결합이 투과에 영향을 미쳤으며 입체인자인 E_s에 의한 영향은 알코올의 분자량이 커짐에 따라 증가되었으나 분자량이 같은 알코올에서는 분자내의 가지가 존재함에 따라 감소되었다.