Functional additives were prepared by grafting polar acrylic acid on nonpolar polyethylene wax which was produced by pyrolysis. The effect of reaction factors on grafting degree was investigated. The grafting degree increased as the molecular weight of polyethylene wax decreased. Although the grafting degree increased as acrylic acid content increased, the grafting degree became lower in case of excess acrylic acid content due to the incompatibility with nonpolar reaction medium. The grafting degree increased as both reaction temperature and reaction time increased because of the increased formation of reaction active sites on polyethylene chains. The radical initiator of longer half life gave the higher grafting degree at the same reaction conditions. Glass transition temperature of grafted polyethylene wax decreased as the grafting degree increased.

열분해 반응을 통해 제조된 비극성 폴리에틸렌 왁스에 대해 극성 아크릴산 단량체를 그래프트 반응시켜 기능성 첨가제를 제조하였고, 반응인자가 그래프트 효율에 미치는 영향을 조사하였다. 폴리에틸렌 왁스의 분자량이 작을수록 그래프트율이 증가하였다. 아크릴산 함량이 증가할수록 그래프트율이 증가하였으나 과량의 아크릴산 함량에서는 비극성 반응물과의 혼화성이 불량하여 그래프트율이 감소하였다. 반응시간이 증가하거나 반응온도가 증가함에 따라 폴리에틸렌 사슬에 그래프트 반응활성점이 증가하여 그래프트율이 향상되었다. 개시제로는 반기가 더 긴 라 디칼 개시제가 동일 반응조건에서 더 높은 그래프트율을 나타내었다. 그래프트율이 증가할수록 그래 트 폴리에틸 렌 왁스의 유리전이온도는 감소하였다.

Keywords: pyrolysis polyethylene wax; graft polymerization; acrylic acid; grafting degree