Curing behavior of silicone rubber modified epoxy resins, which were prepared from the reaction of cycloaliphatic epoxy resins and silicone rubber with amine functional groups, cured in the presence of an anhydride hardener, was studied by differential scanning calorimeter (DSC) and oscillatory rheometer. The rate of cure reaction increased, the heat of cure reaction decreased, and the time of gelation shortened as silicone rubber content was increased until 10 wt%. Isothermal cure results using DSC fitted to the values calculated by the modified Kamal's model well. It is thought that the reactive silicone rubber modified epoxy resins with improved processability as well as flexibility and good weather resistance can be obtained by introducing a small amount of flexible silicone segment to weather resistible cycloaliphatic epoxy network.

지환형 에폭시 수지와 아민기를 함유하고 있는 액상 실리콘 수지의 반응으로 생성된 실리콘 고무 개질 에폭시 수지를 산무수물 경화제를 이용하여 경화시킬 때의 경화거동을 시차주사열량계와 진동 레오미터를 이용하여 연구하였다. 실리콘 고무의 함량이 10 wt%로 증가함에 따라 경화반응속도는 증가하였고 경화반응열은 감소하였으며 젤화시간은 짧아졌다. 등온경화의 결과는 수정된 Kamal 모델과 잘 부합하였다. 소량의 유연한 실리콘 부분을 내후성이 우수한 지환형 에폭시 수지에 첨가함으로써 유연성과 내후성이 우수할 뿐만 아니라 가공성이 개선된 반응성 실리콘고무 개질 에폭시 수지를 얻을 수 있다고 사료된다.

Keywords: silicone rubber; cycloaliphatic epoxy; methyl hexahydrophthalic anhydride; cure kinetics; chemorheology