  • Development of Polydiacetylene-Polydimethylsiloxane Based Chloroform Sensor
  • Park IS, Park DH, Kim JM
  • 폴리다이아세틸렌-폴리다이메틸실록산 기반의 클로로포름 검출센서
  • 박인성, 박동훈, 김종만
Abstract
In this study, we have developed a solvatochromic polydiacetylene(PDA)-embedded polydimethylsiloxane (PDMS) film-type sensor for selective colorimetric detection of chloroform. PDA-PDMS film was readily fabricated by mixing PDA which was derived from 2-methoxyethyl pentacosa-10,12-diynoate (PCDA-EGME) and PDMS precursor. The PDA embedded PDMS film displayed a red (λmax=545 nm) to yellow (λmax=477 nm) colorimetric transition upon exposure to chloroform. The film-type sensor was found to be selective for chloroform among 19 common solvents.

본 연구에서는 용매변색성을 지니는 폴리다이아세틸렌(polydiacetylene, PDA)을 중합하여 이를 함유한 폴리다이메틸실록산(polydimethylsiloxane, PDMS) 기반의 필름센서를 개발하였으며 이를 이용하여 클로로포름에서의 용매변색을 확인하였다. 다이아세틸렌(diacetylene, DA) 단량체인 2-methoxyethyl pentacosa-10,12-diynoate(PCDA-EGME)를 합성하고 저온에서 254 nm UV를 조사하여 PDA를 광 중합한 후, 이를 PDMS에 내포시켜 필름 센서를 제조하였다. 필름형 센서는 적색(λmax=545 nm)을 띠고 있으며, 센서를 클로로포름에 노출시키면 황색(λmax=477 nm)으로 변하는 것을 관찰하였다. 총 19 종의 용매 중 클로로포름에서 선택적으로 변색이 발생하였으며 이를 이미지 분석을 통해 CMYK 중 yellow, magenta 값을 추출하여 차이 값을 분석하였다.

Keywords: polydiacetylene; polydimethylsiloxane; solvatochromism; sensor; chloroform

References
  • 1. Yu G, Gao J, Hummelen JC, Wudl F, Heeger AJ, Science, 270, 5243 (1995)
  •  
  • 2. Janata J, Josowicz M, Nat. Mater., 2(1), 19 (2003)
  •  
  • 3. Jang H, Song K, Kim SH, Polym. Korea, 35(4), 370 (2011)
  •  
  • 4. Bousquet A, Awada H, Hiorns RC, Dagron-Lartigau C, Billon L, Prog. Polym. Sci, 39, 1847 (2014)
  •  
  • 5. McQuade DT, Pullen AE, Swager TM, Chem. Rev., 100(7), 2537 (2000)
  •  
  • 6. Park J, Son Y, Polym. Korea, 38(6), 809 (2014)
  •  
  • 7. Jang G, Seo S, Lee TS, Sens. Actuators B-Chem., 221, 1229 (2015)
  •  
  • 8. Mueller A, O'Brien DF, Chem. Rev., 102(3), 727 (2002)
  •  
  • 9. Ahn DJ, Kim JM, Acc. Chem. Res., 41, 805 (2008)
  •  
  • 10. Lee YH, Yim KH, Heo J, Choi JS, Polym. Korea, 38(1), 43 (2014)
  •  
  • 11. Pumtang S, Siripornnoppakhun W, Sukwattanasinitt M, Ajavakom A, J. Colloid Interface Sci., 364(2), 366 (2011)
  •  
  • 12. Eaidkong T, Mungkarndee R, Phollookin C, Tumcharern G, Sukwattanasinitt M, Wacharasindhu S, J. Mater. Chem., 22, 5970 (2012)
  •  
  • 13. Lee J, Chang HT, An H, Ahn S, Shim J, Kim JM, Nat. Commun., 4, 2461 (2013)
  •  
  • 14. Yang JE, Lee S, Bhak G, Lee M, Jeong DH, Jung S, Paik SR, Sens. Actuators B-Chem., 227, 313 (2016)
  •  
  • 15. Jackman RJ, Wilbur JL, Whitesides GM, Science, 269(5224), 664 (1995)
  •  
  • 16. Heckele M, Schomburg WK, J. Micromech. Microeng., 14, R1 (2004)
  •  
  • 17. Park IS, Heo E, Nam YS, Lee CW, Kim JM, J. Photochem. Photobiol. A-Chem., 238, 1 (2012)
  •  
  • 18. Nam YS, Yoo I, Yarimaga O, Park IS, Park DH, Song S, Kim JM, Lee CW, Chem. Commun., 50, 4251 (2014)
  •  
  • 19. Park DH, Hong J, Park IS, Lee CW, Kim JM, Adv. Funct. Mater., 24(33), 5186 (2014)
  •  
  • 20. Park IS, Park HJ, Kim JM, ACS Appl. Mater. Interfaces, 5, 8805 (2013)
  •  
  • 21. Park IS, Park HJ, Jeong W, Nam J, Kang Y, Shin K, Chung H, Kim JM, Macromolecules, 49(4), 1270 (2016)
  •  
  • 22. Lee JN, Park C, Whitesides GM, Anal. Chem., 75, 6544 (2003)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2016; 40(5): 769-773

    Published online Sep 25, 2016

  • 10.7317/pk.2016.40.5.769
  • Received on May 2, 2016
  • Accepted on Jun 4, 2016