  • Fabrication of a Novel Water Swellable Styrene-butadiene Rubber through the In-situ Polymerization of Lithium Acrylate
  • Jiang X, Xu X, Geng T, You F, Wang W, Yao C
  • 리튬 아크릴레이트의 In-situ 중합을 이용한 수팽윤성 스티렌-부타디엔 고무의 제조
Abstract
A novel water-swellable rubber (WSR) was prepared by blending styrene butadiene rubber (SBR) with dicumyl peroxide (DCP) and unsaturated carboxylic acid salt lithium acrylate (LiAA). The mechanical properties and water absorption behavior of WSR were studied. The results showed that LiAA was developed into polylithiumacrylate (PliAA) during the process of SBR vulcanization through in-situ polymerization, leading to the improvement of the mechanical properties and water absorption performance. The optimum usages of DCP and triallyl isocyanurate (TAIC) to attain the highest water swelling ratio for WSR were 3 and 1 phr, respectively. In addition, the tensile strength and the hardness of WSR were also enhanced by incorporating DCP or TAIC.

Keywords: water swellable rubber; in-situ polymerization; lithium acrylate; water absorption rate

References
  • 1. Jiang XL, Hu K, Yang P, Ren J, Plast. Rubber Compos, 42, 327 (2013)
  •  
  • 2. Choi SS, Ha SH, J. Ind. Eng. Chem., 15(2), 167 (2009)
  •  
  • 3. Zhang ST, Plast. Rubber Compos., 41, 326 (2012)
  •  
  • 4. Ren WT, Peng ZL, Zhang Y, Zhang YX, Polym. Polym. Compos., 13, 181 (2005)
  •  
  • 5. Bajpai AK, Bhanu S, Colloid Polym. Sci., 282, 76 (2003)
  •  
  • 6. Wang GJ, Li M, Chen XF, J. Appl. Polym. Sci., 68(8), 1219 (1998)
  •  
  • 7. Ren WT, Peng ZL, Zhang Y, Zhang YX, J. Appl. Polym. Sci., 92(3), 1804 (2004)
  •  
  • 8. Park JH, Kim D, J. Appl. Polym. Sci., 80(1), 115 (2001)
  •  
  • 9. Lang FZ, Li S, Du FL, Wang ZB, J. Macromol. Sci. B, 52, 1322 (2013)
  •  
  • 10. Karabanova LV, Mikhalovska SV, Sergeeva LM, Meikle ST, Helias M, Lloyd A, Polym. Eng. Sci., 44(5), 940 (2004)
  •  
  • 11. Liu CS, Ding JP, Zhou L, Chen SH, J. Appl. Polym. Sci., 102(2), 1489 (2006)
  •  
  • 12. Hosseinzadeh H, Alijani D, Polym. Korea, 38(5), 588 (2014)
  •  
  • 13. Wang GJ, Li M, Chen XF, J. Appl. Polym. Sci., 72(4), 577 (1999)
  •  
  • 14. Wang L, Zhao SH, Li A, Zhang XY, Polymer, 51(9), 2084 (2010)
  •  
  • 15. Ding NX, Xu SF, Li L, Adv. Mater. Res., 710, 106 (2013)
  •  
  • 16. Matsumoto A, Watanabe K, Aota H, Takayama Y, Kameyama A, Nakanishi T, Polymer, 41(10), 3883 (2000)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2016; 40(5): 684-690

    Published online Sep 25, 2016

  • 10.7317/pk.2016.40.5.684
  • Received on Mar 8, 2016
  • Accepted on Apr 18, 2016