  • Structural, Thermal, and Mechanical Properties of PLA/PBAT/MEA Blend
  • Kim TJ, Kim TH, Kim SG, Seo KH
  • PLA/PBAT/MEA 블렌드의 구조변화 및 열적, 기계적 성질
  • 김태진, 김태희, 김상구, 서관호
Abstract
In this study, a polymer blend of poly(lactic acid) (PLA), poly(butylene adipate-co-terephthalate) (PBAT), and ethanolamine (MEA) (PLA/PBAT/MEA) was prepared. MEA made PLA/PBAT capable of transesterification reaction, acted as a catalyst of coupling reaction and improved the compatibility between PLA and PBAT. The structural and thermal properties of PLA/PBAT/MEA blend were characterized, and PLA/PBAT/MEA blend was used for the coupling agent of PLA/PBAT blend. In conclusion, the PLA/PBAT/MEA blend had an improved compatibility due to chemical coupling and showed a possibility as a coupling agent.

본 연구에서는 poly(lactic acid)(PLA), poly(butylene adipate-co-terephthalate)(PBAT), ethanolamine(MEA) 블렌드를 제작하였다. MEA는 PLA/PBAT의 에스터 치환반응을 가능하게 하였고, 커플링반응의 촉매로써 작용하였으며, PLA와 PBAT간의 상용성을 증진하게 하였다. PLA/PBAT/MEA 블렌드의 구조 및 열적 특성을 관찰하였고, PLA/PBAT/MEA 블렌드를 PLA/PBAT 블렌드의 커플링제로 사용하였다. 결론적으로 PLA/PBAT/MEA 블렌드는 화학적 결합으로 인하여 상용성을 향상하였고, 커플링제로의 가능성을 보여주었다.

Keywords: PLA; PBAT; MEA; coupling agent; transesterification

References
  • 1. Carothers WH, Dorough GL, Van natta FJ, J. Am. Chem. Soc., 54, 761 (1932)
  •  
  • 2. Dorgan J, Lehermeier J, Palade L, Cicero J, Macromol. Symp., 175, 55 (2001)
  •  
  • 3. Jacobsen S, Degee PH, Fritz HG, Dubois PH, Jerome R, Polym. Eng. Sci., 39(7), 1311 (1999)
  •  
  • 4. Sinclair RG, ANTEC, 87, 1214 (1987)
  •  
  • 5. Kricheldorf HR, Kreiser-Saunders I, Macromol. Symp., 103, 85 (1996)
  •  
  • 6. Nampoothiri KM, Nair NR, John RP, Bioresour. Technol., 101(22), 8493 (2010)
  •  
  • 7. Otera J, Esterification, Wiley-VCH, Weinheim, 2003.
  •  
  • 8. Benetti S, Romagnoli R, Derisi C, Spalluto G, Zanirato V, Chem. Rev., 95(4), 1065 (1995)
  •  
  • 9. Riemenschneider W, Bolt HM, Esters Organic Ullmann’s Encyclopedia of Industrial Chemistry, Wiley-VCH, Weinheim, 2005.
  •  
  • 10. Nair V, Bindu S, Sreekumar V, Angew. Chem.-Int. Edit., 43, 5130 (2004)
  •  
  • 11. Toda M, Takagaki A, Okamura M, Kondo JN, Hayashi S, Domen K, Hara M, Nature, 438, 178 (2005)
  •  
  • 12. Yoo DW, Han JH, Nam SH, Kim HJ, Kim C, Lee JK, Inorg. Chem. Commun., 9, 654 (2006)
  •  
  • 13. Stanton MG, Gagne MR, J. Org. Chem., 62, 8240 (1997)
  •  
  • 14. Lin MH, Rajanbabu TV, Org. Lett., 2, 997 (2000)
  •  
  • 15. Hans JJ, Driver RW, Burke SD, J. Org. Chem., 64, 1430 (1999)
  •  
  • 16. Weissermel K, Arpe H, Lindley CR, Hawkins S, Industrial Organic Chemistry, 2nd Edition, Wiley-VCH, Weinheim, 2003.
  •  
  • 17. Occupational Safety & Health Administration. https://www.osha.gov/dts/chemicalsampling/data/CH_239000.html (2012).
  •  
  • 18. Spitalsky Z, Lacik I, Lathova E, Janigova I, Chodak I, Polym. Degrad. Stabil., 91, 856 (2006)
  •  
  • 19. Kim DJ, Min CH, Park HY, Kim SG, Seo KH, Appl. Chem. Eng., 24(1), 104 (2013)
  •  
  • 20. Weng YX, Jin YJ, Meng QY, Wang L, Zhang M, Wang YZ, Polym. Test, 32, 918 (2013)
  •  
  • 21. Ren J, “Biodegradable Poly(Lactic Acid): Synthesis, Modification”, in Processing and Applications, Springer-Verlag, London, 2011.
  •  
  • 22. Asahi Research Center, Handbook of Proton-NMR Spectra and Data-Vol 7, Academic Press, Tokyo, 1985.
  •  
  • 23. Asahi Research Center, Handbook of Proton-NMR Spectra and Data-Vol 8, Academic Press, Tokyo, 1985.
  •  
  • 24. Asahi Research Center, Handbook of Proton-NMR Spectra and Data-Vol 1, Academic Press, Tokyo, 1985.
  •  
  • 25. The Infrared Spectra Atls of Monomers and Polymers, Sadtler Research Labs, Philadelphia, 1984.
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2016; 40(3): 371-379

    Published online May 25, 2016

  • 10.7317/pk.2016.40.3.371
  • Received on Oct 20, 2015
  • Accepted on Feb 22, 2016