  • Preparation and Properties of Coating Materials of Polydimethylsiloxane with Acrylate Groups
  • Bak SW, Kang HJ, Kang DW
  • Acrylate기를 갖는 Polydimethylsiloxane계 코팅 액의 제조와 그 특성
  • 박승우, 강호종, 강두환
Abstract
α,ω-Hydroxypropyl polydimethylsiloxane (HO-PDMS) was prepared by hydrosilylation of hydrogen terminated polydimethylsiloxane with allyl alcohol. Polydimethylsiloxane modified urethane with isocyanate group (PSU) was prepared from cyclic trimer of hexamethylenediisocyanate with HO-PDMS. PDMS modified urethane base resin with acrylic group (PSUA) was prepared from the urethane reaction of PSU with isocyanate group and 2-hydroxyethylmethacrylate. Their structures were characterized using FTIR and NMR. Coating materials were prepared by mixing PSUA, acrylic hardner, photo-initiator, and solvent and coated on PET film to obtain flexible and hard coating film by UV irradiation. Transparency of coating film was 89.7%, contact angle, 88°, and pencil hardness, 3H.

α,ω-Hydroxypropyl기를 갖는 polydimethylsiloxane을 합성하고 이를 hexamethylenediisocyanate(HDI)의 고리화 반응으로 제조된 HDI trimer와 반응시켜 말단에 이소시아네이트 기를 갖는 PDMS 변성 urethane(PSU)을 제조하였다. 이소시아네이트기를 갖는 PSU와 2 - hydroxyethylmethacrylate를 urethane 반응으로 acrylate기를 갖는 PDMS 변성 urethane base 수지(PSUA)를 제조하였으며, 이를 FTIR, NMR로 구조를 확인하여 분석하였다. 제조한 base 수지에 아크릴계 경화제, 광 개시제, 용매들을 혼합하여 코팅 액을 제조하였으며 이를 PET 필름에 도포하고 자외선으로 조사하여 고경도의 유연성을 갖는 코팅 막을 얻었다. 얻어진 코팅 막의 광 투과도는 89.7%, 연필경도는 3H, 접촉각은 88° 였다.

Keywords: hydroxypropylpolydimethylsiloxane; hexamethylenediisocyanate; coating material; pencil hardness.

References
  • 1. Peinado C, Salvador EF, Baselga J, Catalina F, Macromol. Chem. Phys., 202, 1924 (2001)
  •  
  • 2. Zhang JY, Windall G, Boyd IW, Appl. Surf. Sci., 186(1-4), 568 (2002)
  •  
  • 3. Decker C, Viet TNT, Decker D, Weber-Koehl E, Polymer, 42(13), 5531 (2001)
  •  
  • 4. Paul S, Editor, Surface Coatings: Science & Technology, John Wiley & Sons Ltd, England (1996)
  •  
  • 5. Zorll U, Editor, European Coatings Handbook, Vincentz Berlag, Germany (2000)
  •  
  • 6. LI H, Zhang ZB, Hu CP, Wu SS, Ying SK, Eur. Polym. J., 40, 2195 (2004)
  •  
  • 7. Chuyin Z, Xingyuan Z, Jiabing D, Chenyan B, Prog. Org. Coat., 63, 238 (2008)
  •  
  • 8. Kojima S, Polym. Eng. Sci., 33, 253 (1993)
  •  
  • 9. Yilgor I, Wilkes GL, McGrath JE, Polym. Prep., 24, 80 (1983)
  •  
  • 10. Iojoiu C, Abadie MJM, Harabagiu V, Pinteala M, Simionescu BC, Eur. Polym. J., 36, 2115 (2000)
  •  
  • 11. Nabeth B, Gerard JF, Pascault JP, J. Appl. Polym. Sci., 60(12), 2113 (1996)
  •  
  • 12. Choi JH, Kim HJ, J. Ind. Eng. Chem., 12(3), 412 (2006)
  •  
  • 13. Naghash HJ, Mallakpour S, Mokhtarian N, Prog. Org. Coat., 55, 375 (2006)
  •  
  • 14. Tang C, Liu W, Ma S, Wang Z, Hu C, Prog. Org. Coat., 10, 1016 (2010)
  •  
  • 15. Joe YG, Lee JW, Kim JY, Suh KD, Appl. Chem., 2(2), 616 (1998)
  •  
  • 16. Andrzejewska E, Prog. Polym. Sci., 26, 605 (2001)
  •  
  • 17. Elsvernd CS, Spinu M, Krukonis VJ, Gallagher PM, Mohanty DK, McGrath JE, Silicone-based Polymer Science, American Chemical Society, Washington, p.145 (1990)
  •  
  • 18. Lee BC, Kang DW, Polymer, 28, 143 (2004)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2014; 38(2): 138-143

    Published online Mar 25, 2014

  • Received on Aug 12, 2013
  • Accepted on Nov 1, 2013