A brominated epoxy resin was prepared from tetrabromobisphenol A and epichlorohydrin, and further modified with phosphorus containing compounds to produce resins with different phosphorus contents. From the thermogravimetric analysis, it was found that the thermal stability of the modified resin decreased with the increase in phosphorus contents. The commercial epoxy resin was flame-retarded using the phosphorus- and bromo-containing resin. It showed an excellent self-extinguishing property and met Underwriters Laboratory Specification 94 VO grade. When the commercial epoxy resin was mixed with 10 part of modified resin and 10 part of antimony oxide, the oxygen index was 34.5. This value is much higher than that of commercial epoxy resin, 21.5.

Tetrabromobisphenol A와 epichlorohydrin으로부터 브롬화 에폭시수지를 합성하였으며 이것을 인함유 화합물과 반응시켜 인의 함량이 다른 수지를 얻었다. 열중랴분석으로 이 변성수지의 열안정성이 인함량의 증가에 따라 감소함을 확인하였다. 시판 에폭시수지를 인과 브롬을 함유한 수지로 난연화시킨 결과 이 수지는 우수한 자기소화성을 나타내었으며 UL규격 94VO등급에 합격하였다. 이 변성 에폭시수지와 산화안티몬을 각각 10부씩 시판 에폭시수지에 혼합할 경우 Oxygen Index는 34.5를 나타내었다. 이 수치는 시판 에폭시수지의 Oxygen Index 21.5보다 훨씬 높았다.