Water permeation, solute separation and blood compatibility of poly-γ-methyl-L-glutamate(PMLG) membranes were investigated. IR spectra study indicates that molecular chains in the prepared membrane exist in the α-helical conformation. Permeation experiments showed that water flux increased linealy with increasing both applied temperature and pressure. Activation energy calculated from the slope of Arrhenius plot of hydraulic permeability K_ω of the membrane was found to be 9.16 Kcal/mole. The result of solute separation through PMLG membrane indicates that solute having molecular weight of more than 20,000 did not permeate. The PMLG membrane showed a good performance when the casting temperature and annealing temperature was in the range of 50℃ and 60℃. Blood compatibility of the polymer has also been discussed.

poly-γ-methyl-L-glutamat(PMLG) 막의 투수성, 수용성용질의 분리성능 및 혈액적합성을 검토하였다. 제조한 막의 상태에서 분자사슬은 α-helix구조를 취하고 있음을 IR로 확인하였다. 투수성 실험결과 투수성은 온도의 상승과 압력이 증가함에 따라 직선적으로 증가하였으며 유체역학적 투과계수 K_ω를 Arrhenius plot하여 그 기울기로부터 활성화에너지 9.16 Kcal/mole을 얻었다. 용질배제율 실험에서 분자량 20,000 이상인 용질은 거의 투과하지 않음을 알았다. 막성능은 제막온도와 열처리온도가 50∼60℃인 범위에서 우수하였다. 또한 PMLG의 혈액적합성도 아울러 검토하였다.