In order to develop the blends with good long-term thermal stability and tensile elongation, the blends of polyphenylene sulfide (PPS) and 7 kinds of elastomer were tested. PPS/elastomer (90/10, 80/20, 70/30) blend samples were prepared by compression molding after twin screw extrusion or punching after sheet extrusion. Rheological, mechanical property and morphology of the blends were analyzed by capillary rheometer, UTM, impact tester, and SEM. For long-term thermal stability tests, the mechanical properties were measured again after the samples were stored in a convection oven for a week. The tensile strengths were almost same regardless of kinds of elastomer and the tensile elongation was the maximum for the PPS/m-EVA blend. As the content of elastomer increased, the elongation increased but delamination occurred at 30 wt% of elastomer content. The tensile strength increased but the elongation decreased seriously after thermal aging. Many problems related with PPS processing could be solved by adding a small amount of the elastomers partially compatibile with PPS and it would be applicable to develop various PPS grades.

장기내열성과 파단신율이 우수한 블렌드 수지를 개발하고자 polyphenylene sulfide(PPS)에 7종류의 elastomer 를 용융혼합하여 그 가능성을 조사해 보았다. PPS/elastomer(90/10, 80/20, 70/30) 블렌드를 제조한 후 시험편을 압축성형 또는 sheet를 제조하여 capillary rheometer, UTM, impact tester, SEM 등으로 유변학적 거동, 기계적 특성 및 모폴로지를 측정하였고 오븐에서 일주일간 열을 가한 후 다시 기계적 특성을 측정하였다. 열을 가하기 전의 인장강도는 elastomer 종류에 관계없이 비슷하였고 파단신율은 m-EVA의 경우가 가장 큰 값을 보였다. Elastomer 첨가량을 증가시킴에 따라 신율이 증가하였는데 30 wt%정도 첨가 시 박리가 발생하였다. 오븐테스트 이후에는 인장강도는 더 증가한 반면에 신율은 급격히 감소하였다. 상기의 elastomer들이 PPS와 부분적인 상용성이 있는 것으로 보이는 바 소량의 elastomer 첨가 만으로도 PPS 가공과 관련된 여러 문제 등을 해결할 수 있어 다양한 그레이드의 개발에 적극 활용될 수 있을 것으로 기대된다.

Keywords: polyphenylene sulfide; elastomer; thermal stability; elongation; blends.