  • Effect of pH-Sensitive P(MAA-co-PEGMA) Hydrogels on Release and Stability of Albumin
  • Yang J, Kim B
  • pH 감응성 P(MAA-co-PEGMA) 수화젤이 알부민의 방출과 안정성에 미치는 영향
  • 양주승, 김범상
Abstract
pH-sensitive P(MAA-co-PEGMA) hydrogel particles were prepared and their feasibility as smart delivery carriers for cosmetic ingredients was evaluated. P(MAA-co-PEGMA) hydrogel particles having an average size of approx. 2 μm were synthesized via dispersion photopolymerization. There was a drastic change in the swelling ratio of P(MAAco-PEGMA) particles at a pH of around 5 due to the ionization of MAA in the hydrogel and as the amount of MAA in the hydrogel increased, the swelling ratio increased at a pH above 5. The P(MAA-co-PEGMA) hydrogel particles showed a pH-sensitive release behavior. Thus, at pH 4 almost none of the albumin permeated through the skin while at pH 6 relatively high skin permeability was obtained. The albumin loaded in the P(MAA-co-PEGMA) hydrogel particles was hardly degraded in the presence of pepsin and its stability was maintained.

본 연구에서는 pH 감응성 수화젤 입자를 이용하여 외부환경에 불안정한 활성물질을 화장품 제형 내에서는 안정하게 보존하고, 피부에 도포 시 빠른 방출로 피부에 흡수될 수 있는 지능형 전달시스템의 구현 가능성을 확인하기 위하여, 분산광중합을 이용하여 pH 감응성을 가지는 P(MAA-co-PEGMA) 수화젤 입자를 평균 크기 약 2 μm의 구형 입자로 합성하였다. 합성된 P(MAA-co-PEGMA) 수화젤 입자는 수화젤의 MAA에 존재하는 카르복시기의 이온화에 의하여 pH 5를 전후로 한 급격한 팽윤비의 변화를 보여주었다. pH에 따른 수화젤 내부에 탑재된 알부민의 방출 및 피부투과 실험결과, P(MAA-co-PEGMA) 수화젤 입자는 pH 4.0에서는 소량의 알부민이 방출되어 피부투과가 거의 일어나지 않은 반면, pH 6.0에서는 초기부터 다량의 알부민이 방출되어 상대적으로 높은 피부투과율을 나타내었다. 펩신을 이용한 알부민의 안정성 실험결과, P(MAA-co-PEGMA) 수화젤은 내부에 탑재된 알부민을 외부환경으로부터 보호하여 알부민의 안정성을 유지시켜 주었다.

Keywords: pH-sensitive; hydrogel particles; albumin stability; smart delivery system; skin permeability.

References
  • 1. Peppas NA, Bures P, Leobandung W, Ichikawa H, Eur. J.Pharm. Biopharm., 50, 27 (2000)
  •  
  • 2. Chung BG, Lee KH, Khademhosseini A, Lee SH, Lab Chip., 12, 45 (2012)
  •  
  • 3. Gonzalez-Chomon C, Concheiro A, Alvarez-Lorenzo C, Materials., 4, 1927 (2011)
  •  
  • 4. Cabral J, Moratti SC, Future Med. Chem., 3, 1877 (2011)
  •  
  • 5. Jabbari E, Curr. Opin. Biotechnol., 22, 655 (2011)
  •  
  • 6. Jeong B, Kim SW, Bae YH, Adv. Drug Deliv. Rev., 54, 37 (2002)
  •  
  • 7. Tomatsu I, Peng K, Kros A, Adv. Drug Deliv. Rev., 63, 1257 (2011)
  •  
  • 8. Li Z, Guan J, Expert Opin. Drug Deliv., 8, 991 (2011)
  •  
  • 9. Zha L, Banik B, Alexis F, Soft Matter., 7, 5908 (2011)
  •  
  • 10. Bajpai AK, Bajpai J, Saini R, Gupta R, Polym. Rev., 51, 53 (2011)
  •  
  • 11. Foss AC, Goto T, Morishita M, Peppas NA, Eur. J.Pharm. Biopharm., 57, 163 (2004)
  •  
  • 12. Mocanu G, Mihai D, Dulong V, Picton L, Le Cerf D, Carbohydr. Polym., 87, 1440 (2012)
  •  
  • 13. Kim B, Kim SH, Ryoo W, J. Biomater. Sci.-Polym. Ed., 20, 427 (2009)
  •  
  • 14. Lee E, Kim B, Polym. Bull., 67(1), 67 (2011)
  •  
  • 15. Wood KM, Stone GM, Peppas NA, Acta Biomater., 6, 48 (2010)
  •  
  • 16. Zhang SG, Nat. Mater., 3(1), 7 (2004)
  •  
  • 17. Revzin A, Russell RJ, Yadavalli VK, Koh WG, Deister C, Hile DD, Mellott MB, Pishko MV, Langmuir, 17(18), 5440 (2001)
  •  
  • 18. Zhu J, Marchant RE, Expert Rev. Med. Devices., 8, 607 (2011)
  •  
  • 19. Kligman AM, Papa CM, J. Soc. Cosmetic Chemists., 16, 557 (1965)
  •  
  • 20. Peters T, All about Albumin: Biochemistry, Genetics, and Medical Applications, Academic Press, New York (1996)
  •  
  • 21. Jiang R, Hayden CGJ, Prankerd RJ, Roberts MS, Benson HAE, J. Chromatogr. B., 682, 137 (1996)
  •  
  • 22. Hasse S, Kothari S, Rokos H, Kauser S, Schurer NY, Schallreuter KU, Exp. Dermatol., 14, 182 (2005)
  •  
  • 23. Kerr A, Ferguson J, Photodermatol. Photoimmunol.Photomed., 26, 56 (2010)
  •  
  • 24. Sharma V, Jaishankar A, Wang YC, McKinley GH, Soft Matter., 7, 5150 (2011)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2013; 37(3): 262-268

    Published online May 25, 2013

  • Received on Aug 7, 2012
  • Accepted on Dec 24, 2012