Experimental results of compressive modulus for rigid polyurethane foams were compared with the modified Kerner''s equation applicable to foam and the Rusch''s empirical equation. The results showed that the modified Kerner''s equation was applicable only to >0.8 volume fraction of polymer. However the Rusch''s empirical equation followed well with the measured values for all volume fraction of polymer examined. To derive a suitable equation for the foam filled with mica, a plate type filler, the Padawer''s equation for mica-reinfored composites and Rusch''s empirical equation were combined. As the mica content was increased, however, the experimental values of the compressive modulus showed much smaller values than those calculated by the combined equation. To correct the difference of those values, especially at higher mica content, a parameter K was introduced. The result showed K value in the range of 0.05∼0.29. The mica-filled foams showed higher compressive modulus than the CaCo ₃-filled foams at the same filler content.

Kerner의 이론식을 미보강 foam의 압축 modulus에 적용할 수 있도록 변형한 수정식파 Rusch의 실험식을 실험결과와 비교하였다. Kerner의 수정식은 수지의 체적분율로 0.8이상일 때는 잘 적용되었지만 0.82%이하에서는 적용되지 않았다. 그러나 Rusch의 실험식은 전체적분율 범위에서 걸쳐서 실험결과와 일치하였다. 판장충전재를 matrix안에 충전시킬 때의 Padawer의 강도식과 foam에 적용이되는 Rusch식을 복합하여 복합식을 유도하였다. 이 복합이론식에 의한 이론치와 실측치를 비교한 결과 mica의 체적분율이 증가할수록 실측치가 이론치보다 현저히 낮아짐을 알았다. 이론치와 실측치사이의 차를 보강하기 위한 변수 K를 설정하여 그값을 구했는데 K는 0.05∼0.29 범위에 있었다. 또한 동량의 mica와 Calcium Carbonate를 foam에 각각 충전시켜 압축탄성률을 측정한 결과 판장충전재인 Calcium이 입상충전재인 Carbonate보다 큰 값을 나타냈다.