Liquid crystalline aromatic polyesters (LCPs) are representative examples of thermotropic liquid crystalline polymers, whose structure-property relationships have been the subject of many researches. In this study, we synthesized organo-soluble liquid crystalline aromatic polyesters, and their composites with acetylene-terminated thermoset resins were prepared and characterized. Soluble LCPs were synthesized by employing 6-hydroxy-2-naphthoic acid, terephthalic acid, isophthalic acid, and 4-aminophenol as monomers via condensation polymerization based on transesterfication and transamidation. Acetylene-terminated thermoset resins were synthesized by the reaction of 4-ethynylaniline with terephthaloyl dichloride, isophthaloyl dichloride or 4,4′-biphenyldicarbonyl dichloride. We prepared the soluble LCP/thermoset composites by solution blending followed by thermal treatment. The thermal stability, thermal expansion coefficient, and dielectric properties of the composite were studied.

방향족 액정 폴리에스테르는 열방성 액정 중합체의 대표적인 예로 지금까지 구조-물성 관계가 많이 연구되었다. 본 연구에서는 유기 용매에 녹일 수 있는 가용성 방향족 액정 폴리에스테르를 합성하고 아세틸렌 말단기를 갖는 열경화성 수지와 복합화하여 제반 물성을 비교하였다. 가용성 방향족 액정 폴리에스테르는 6-hydroxy-2-naphthoic acid, terephthalic acid, isophthalic acid 및 4-aminophenol을 단량체로 하여 에스테르 및 아미드 교환 반응에 기초로 한 축합 중합법을 이용하여 합성하였다. 아세틸렌 말단기를 갖는 열경화성 수지는 4-ethynylaniline과 terephthaloyl dichloride, isophthaloyl dichloride, 4,4′-biphenyldicarbonyl dichloride 등과 각각 반응시켜 합성하였다. 가용성 방향족 액정 폴리에스테르와 열경화성 수지를 용액 블렌딩하고 열처리하여 복합체를 제조하였으며, 복합체의 열적 안정성, 열팽창계수, 유전특성 등을 조사하였다.

Keywords: liquid crystalline polyester (LCP); liquid crystalline thermoset (LCT); polycondensation,composite.