  • Synthesis, Film Fabrication, and Optical Properties of Polymers Containing Metal Cation Complex Type D-π-A Chromophore
  • Jeong S, Kim H, Yoon KB, Han YS, Fujiki M, Takagi A, Kwak G
  • 금속 양이온 배위형 D-π-A 발색단을 포함하는 폴리머의 합성 및 박막화와 광학특성
  • 정선주, 김혜련, 윤근병, 한윤수, 후지키 미치야, 타카기 아키코, 곽기섭
Abstract
Donor-π-acceptor (D-π-A) type chromophore-based polymers were newly synthesized. These polymers exhibited absorption peak due to intramolecular charge transfer (ICT) in a visible range as well as absorption peak due to carbonyl group in both solution and film state by measuring UV visible spectra. The addition of Eu3+ ion into the polymers induced red-shift in absorption due to ICT and the color changes from yellow to red in the solution and film were observed by naked eyes. The contents of crosslinking agent influenced the features and solubility of the polymers. In addition, the contents of crosslinking agent and the Eu3+ ion addition improved film-forming ability.

분자내 전하이동(intramolecular charge transfer, ICT)이 가능한 도너-π-억셉터(D-π-A)타입의 발색단 을 근간으로 한 폴리머를 신규 합성하였다. 이 폴리머는 UV-visible spectra 측정결과 용액 상태에서 뿐만 아니라 고체박막 상태에서도 카르보닐기(carbonyl group)에서 기인하는 흡수와 함께 ICT에 의한 장파장 영역에서의 흡수가 관찰되었다. Eu3+ 이온의 첨가에 의해 장파장영역에서 일어나는 흡수의 적색이동(red shift)을 유도하였으며, 더불어 용액과 박막의 색상도 황색에서 적색으로 변화하는 것이 관찰되었다. 합성된 고분자의 형태 및 유기 용매에 대한 용해도는 가교제의 함량에 따라 다양한 특성을 나타내었다. 또한, 첨가된 가교제의 함량과 Eu3+ 이온의 첨가는 성막 특성의 향상을 유도하였다.

Keywords: D-π-A chromophore; polymer; intramolecular charge transfer (ICT); crosslinker; metal complex

References
  • 1. Burland DM, Miller RD, Walsh CA, Chem. Rev., 94(1), 31 (1994)
  •  
  • 2. Kanis DR, Ratner MA, Marks TJ, Chem. Rev., 94(1), 195 (1994)
  •  
  • 3. Alain V, Blanchard-Desce M, Ledoux I, Zyss J, Chem. Commun., 353 (2000)
  •  
  • 4. Lin W, Ma L, Evans OR, Chem. Commun., 2263 (2000)
  •  
  • 5. Aqad E, Leriche P, Mabon G, Gorgues A, Khodorovsky V, Org. Lett., 3, 2329 (2001)
  •  
  • 6. Jayaprakash KN, Ray PC, Matsuoka I, Bhadbhade MM, Puuranik VG, Nishihara H, Sarkar A, Organometallics, 18, 3851 (1999)
  •  
  • 7. Muller TJJ, Netz AA, Ansorge M, Schmalzlin E, Brauchle C, Meerholz K, Organometallics, 18, 5066 (1999)
  •  
  • 8. Kanis DR, Ratner MA, Marks TJJ, J. Am. Chem. Soc., 114, 10338 (1992)
  •  
  • 9. Jeon YM, Kim JG, Jang JG, Chang HJ, Kim YS, Gong MS, Polym.(Korea), 30(5), 426 (2006)
  •  
  • 10. Lee JH, Lee KS, Polym.(Korea), 25(6), 803 (2001)
  •  
  • 11. Pasini D, Righetti PP, Rossi V, Org. Lett., 4, 23 (2002)
  •  
  • 12. Desimoni G, Faita G, Ricci M, Righetti PP, Tetrahedron, 54, 9581 (1998)
  •  
  • 13. Kwak G, Takagi A, Fujiki M, Macromolecules, 38, 4169 (2004)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2010; 34(4): 376-380

    Published online Jul 25, 2010

  • Received on Apr 5, 2010
  • Accepted on May 15, 2010