Article
  • Preparation and Release Property of Alginate Beads Immobilizing Poly(N-isopropylacrylamide-co-dimethylamino ethyl methacrylate)
  • Kang MK, Kim JC
  • Poly(N-isopropylacrylamide-co-dimethylamino ethyl methacrylate)가 고정화된 알지네이트 비드 제조 및 방출 특성
  • 강미경, 김진철
Abstract
Alginate beads were prepared using poly(N-isopropylacrylamide-co-dimethylamino ethyl methacrylate)(P(NIPAM-co-DMAEMA)). First, P(NIPAM-co-DMAEMA) was immobilized on the surface of alginate beads by taking advantage of electrostatic interaction between alginate and P(NIPAM-co-DMAEMA). Second, P(NIPAM-co-DMAEMA) was contained in the matrix of alginate beads. P(NIPAM-co-DMAEMA) were prepared by a free radical polymerization at 74 ℃ for 12 h. The weight ratio of NIPAM to DMAEMA monomer was 95/5. The copolymer was identified by 1H-NMR. Releases from the alginate beads were observed at 30, 37, and 45 ℃ using blue dextran or FITCdextran(fluorescein isothiocyanate-dextran) as a model drug. The effect of temperature on the degree of release from the beads was insignificant. FITC-dextran was released more than blue dextran possibly due to its smaller molecular weight.

Poly(N-isopropylacrylamide-co-dimethylamino ethyl methacrylate)(P(NIPAM-co-DMAEMA))가 고 정화된 알지네이트 비드를 제조하였다. 알지네이트와 P(NIPAM-co-DMAEMA)의 정전기적 인력을 이용하여 P(NIPAM-co-DMAEMA)로 코팅된 알지네이트 비드와 P(NIPAM-co-DMAEMA)을 함유한 알지네이트 비드를 제조하였다. P(NIPAM-co-DMAEMA)은 자유 라디칼 반응으로 제조하였고 핵자기 공명분광기를 통해 확인하였다. 비드의 온도 민감성 방출 거동을 관찰하였으며, 모델시약으로 blue dextran과 fluorescein isothiocyanate-dextran을 사용하였다. P(NIPAM-co-DMAEMA)가 고정화된 알지네이트 비드로부터의 방출 정도는 온도 의존성이 낮았고, 방출모델시약의 분자량이 작을수록 더 높았다.

Keywords: alginate beads; N-isopropylacrylamide; dimethylamino ethyl methacrylate; release property

References
  • 1. Pillay V, Fassihi R, J. Control. Rel., 55, 243 (1999)
  •  
  • 2. Kim SR, Yuk SH, Jhon MS, Eur. Polym. J., 33, 1009 (1997)
  •  
  • 3. Ertesvag H, Valla S, Polym. Degrad. Stabil., 59, 85 (1998)
  •  
  • 4. Vos PD, Haan BD, Schilfgaarde RV, Biomaterials, 18, 273 (1997)
  •  
  • 5. Choi JH, Lee HY, Kim JC, J. Appl. Polym. Sci., 110(1), 117 (2008)
  •  
  • 6. Roux E, Passirani C, Scheffold S, Benoit JP, Leroux JC, J. Control. Rel., 94, 447 (2004)
  •  
  • 7. Kim MH, Kim JC, Lee HY, Kim JD, Yang JH, Colloid Surf. B-Biointerfaces, 46, 57 (2005)
  •  
  • 8. Han HD, Choi MS, Hwang TW, Song CK, Seong HS, Kim TW, Choi HS, Shin BC, J. Pharm. Sci., 95, 1909 (2006)
  •  
  • 9. Cheng CJ, Chu LY, Zhang J, Zhou MY, Xie R, Desalination, 234(1-3), 184 (2008)
  •  
  • 10. Yamashita K, Nishimura T, Nango M, Polym. Adv. Technol., 14, 189 (2003)
  •  
  • 11. Duracher D, ElaoEssari A, Pichot C, Colloid Polym. Sci., 277, 905 (1999)
  •  
  • 12. Zhang H, Chu LY, Li YK, Lee YM, Polymer, 48(6), 1718 (2007)
  •  
  • 13. Yin W, Chen M, Lu T, Akashi M, Huang X, Eur. Polym. J., 42, 2523 (2006)
  •  
  • 14. Shi J, Alves NM, Mano JF, J. Biomed. Mater. Res. Part B, 84, 595 (2008)
  •  
  • 15. Kono K, Nakai R, Morimoto K, Takagishi T, Biochim. Biophys. Acta., 1416, 239 (1999)
  •  
  • 16. Hayashi H, Kono K, Takagishi T, Biochim. Biophys. Acta., 1280, 127 (1996)
  •  
  • 17. Kim JC, Bae SK, Kim JD, Biochem., 121, 15 (1997)
  •  
  • 18. Kono K, Henmi A, Yamashita H, Hayashi H, Takagishi T, J. Control. Rel., 59, 63 (1999)
  •  
  • 19. Choi JH, Lee HY, Kim JC, Kim YC, J. Ind. Eng. Chem., 13(3), 380 (2007)
  •  
  • 20. Hua JD, Liu YF, Hu J, Wang QQ, Gong ZB, Guo XZ, J. Appl. Polym. Sci., 74(10), 2457 (1999)
  •  
  • 21. Choi JH, Lee HY, Kim JC, J. Appl. Polym. Sci., 108(6), 3707 (2008)
  •  
  • 22. Zhang J, Xie R, Zhang SB, Cheng CJ, Ju XJ, Chu LY, Polymer, 50, 2516 (2009)
  •  
  • 23. Feil H, Bae YH, Feijen J, Kim SW, Macromolecules, 26, 2496 (1993)
  •  
  • 24. van Tomme SR, van Steenbergen MJ, de Smedt SC, van Nostrum CF, Hennink WE, Biomaterials, 276, 2129 (2005)
  •  
  • 25. Yang X, Lee HY, Kim JC, J. Macromol. Sci. Part A-Pure Appl. Chem., 46, 959 (2009)
  •  
  • 26. Karlsson D, Zacchi G, Axelsson A, Biotechnol. Prog., 18(6), 1423 (2002)
  •  
  • 27. Ende MT, Peppas NA, J. Control. Rel., 48, 47 (1997)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2010; 34(1): 79-83

    Published online Jan 25, 2010

  • Received on Oct 6, 2009
  • Accepted on Nov 5, 2009