Article
  • Polymerization and Effect of Organic/Organic Core Shell Binder
  • Sim MK, Ban JE, Kim MS, Seul SD
  • Organic/Organic Core Shell 바인더의 중합과 처리영향
  • 심민기, 반지은, 김민성, 설수덕
Abstract
Core shell binder of organic/organic pair that has two different properties within a particle were prepared by a step emulsion polymerization of methacrylate(MMA), styrene(St), ethyl acrylate(EA), butyl acrylate(BA), and 2-HEMA by using an water soluble initiator(APS) in the presence of an anionic surfactant(SDBS). Unwoven tensile strength of the core shell binder after processing and measuring the PSt/PMMA/2-HEM core shell with the binder is a value represents the highest was 10.75 kgf/2.5 cm, elongation measurements PEA/PBA core shell binder showed the highest value was 120.00%. In conclusion, using the core shell binders were able to control the mechanical properties such as tensile strength and elongation.

아크릴계 단량체인 MMA, St, EA, BA 및 관능성 단량체인 2-HEMA 단량체를 수용성 개시제인 APS와 음이온 유화제인 SDBS를 사용하여 한 입자 내에 서로 다른 물성을 나타내는 core shell 구조의 바인더를 중합후 부직포에 처리하여 기계적 물성을 평가하였다. Core shell 바인더 중합시 단량체 조성에 관계없이 개시제는 1.0 wt%/단량체의 농도를 가지는 APS와 0.04 wt%/단량체의 유화제를 사용했을 때 가장 높은 전환율을 나타내었고, core shell 바인더의 유리전이온도는 공중합체의 단일 전위 곡선에 비하여 core shell 바인더는 2개 이상의 전이 곡선을 얻었다. 부직포에 core shell 바인더를 처리 후 인장강도 및 신장율 측정에서 관능성 단량체를 사용한 PSt/PMMA/2-HEMA core shell 바인더가 10.75 kgf/2.5 cm로 가장 높은 값을 나타내었고, 신장율 측정에는 PEA/PBA core shell 바인더가 120.00%로 가장 높은 값을 나타내었다. 결론적으로 core shell 바인더를 사용하여 부직포의 기계적 물성을 조절할 수 있었다.

Keywords: core shell; particle size; tensile strength; emulsion polymerization

References
  • 1. Cho K, Polymer, 39, 14 (1998)
  •  
  • 2. Ahn TO, Hwang TW, Jho JY, Polym.(Korea), 21(2), 289 (1997)
  •  
  • 3. Lee KC, Polym.(Korea), 21(3), 383 (1997)
  •  
  • 4. Vazquez F, Polym. Int., 41, 1 (1996)
  •  
  • 5. Patsiga R, Litt M, Stannett V, J. Phys. Chem., 64, 801 (1960)
  •  
  • 6. Hughes LJ, Brown GL, J. Appl. Polym. Sci., 5, 580 (1961)
  •  
  • 7. Morgan LW, J. Appl. Polym. Sci., 27, 2033 (1982)
  •  
  • 8. Matsumoto T, Okubo M, Imai T, Kobunshi Ronbunshu, 31, 576 (1974)
  •  
  • 9. Matsumoto T, Okubo M, Imai T, Kobunshi Ronbunshu, 33, 575 (1976)
  •  
  • 10. Okubo M, Katsuta Y, Matsumoto T, Kobunshi Ronbunshu, 36, 459 (1979)
  •  
  • 11. Lee SR, Seul SD, Korean J. Chem. Eng., 19(2), 318 (2002)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2008; 32(5): 470-477

    Published online Sep 25, 2008

  • Received on May 16, 2008
  • Accepted on Jul 1, 2008