  • Synthesis of Polyurethane Nanocomposite Filled Inorganic Particles and Their Properties
  • Son B, Hwang TS
  • 무기입자를 충전한 폴리우레탄 나노복합체의 합성 및 물성
  • 손복기, 황택성
Abstract
The nanocomposites with inorganic nano powder, improved thermal stability, were prepared by urethane polymerization. The structure and surface properties of the nanocomposites were determined by X-ray diffraction and FT-IR, respectively. The thermal stabilities were studied using TGA and DSC. Their morphologies and mechanical properties were observed by SEM and UTM. As a result, the nanocomposites with MMT led to the increase of the silicate layers. The distance between layers of the nanacomposites with MMT was increased by 7.5 A and the new peaks at 1038 cm-1 were shown in the presence of the Si-O groups on the silica. The thermal stabilities of the nanocomposites were higher than those of pore polyurethane matrix. The nanocomposites had higher in mechanical properties than the pure polyurethane matrix.

본 연구는 열안정성을 향상시킨 무기나노 분말충전 나노복합재료를 우레탄 중합방법으로 제조하였다. 나노복합재료의 구조와 표면 특성은 XRD와 FT-IR을 통하여 알아보았고, 열안정성은 TGA와 DSC를 통하여 알아보았으며, SEM을 이용하여 복합재료의 모폴로지를 관찰하였다. 복합재료의 기계적 물성은 UTM을 사용하여 측정하였다. 실험 결과, MMT를 충전한 나노복합재료의 층간거리가 7.5 A 증가하였고, Silica 내 Si-O기에 의해 1038 cm-1에서 새로운 피크가 나타났다. 또한 열안정성과 기계적 물성도 폴리우레탄 매트릭스보다 향상된 것을 확인할 수 있었다.

Keywords: nanocomposite; polyurethane; nano inorganic filler

References
  • 1. Saxena PK, Raut KG, Srinivasan SR, Sivaram S, Rawat RS, Jain RK, Constr. Build. Mater., 5, 208 (1991)
  •  
  • 2. Chew MYL, Zhou X, Tay YM, Polym. Test, 20, 87 (2001)
  •  
  • 3. Tang YW, Santerre JP, Labow RS, Taylor DG, J. Appl. Polym. Sci., 62(8), 1133 (1996)
  •  
  • 4. Tonelli C, Trombetta T, Scicchitano M, Castiglioni G, J. Appl. Polym. Sci., 57(9), 1031 (1995)
  •  
  • 5. Boxhammer J, Polym. Test, 20, 719 (2001)
  •  
  • 6. Noh MH, Lee DC, J. Appl. Polym. Sci., 74(12), 2811 (1999)
  •  
  • 7. Krishnamoorti R, Vaia RAPolymer Nanocomposites, ACS symposium series 804, American Chemical Society, Washington, D C., p.7 (2002)
  •  
  • 8. Pandya MV, Deshpande DD, Hundiwale DG, J. Appl. Polym. Sci., 32, 4959 (1986)
  •  
  • 9. Aranda P, Ruiz-Hitzky E, Chem. Mater., 4, 1395 (1992)
  •  
  • 10. Maiti P, Batt CA, Giannelis EP, Polym. Mater. Sci. Eng., 88, 58 (2003)
  •  
  • 11. Alexandre M, Dubois D, Mater. Sci. Eng., 28, 1 (2000)
  •  
  • 12. Chen TK, Tien YI, Wei KH, Polymer, 41(4), 1345 (2000)
  •  
  • 13. Reegen SL, J. Appl. Polym. Sci., 10, 1247 (1966)
  •  
  • 14. David DJ, Staley HBAnalytical Chemistry of Polyurethane, Wiley-Interscience, New York (1969)
  •  
  • 15. Hernandez-Paron G, Lima RM, Nava R, Garcia-Garduno MV, Castano VM, Adv. Polym. Technol., 21, 116 (2002)
  •  
  • 16. Gilman JW, Jackson CL, Morgan AB, Harris RH, Chem. Mater., 12, 1866 (2002)
  •  
  • 17. An YU, Chang JH, Park YH, Park JM, Polym.(Korea), 26(3), 381 (2002)
  •  
  • 18. Park SJ, Cho KS, Zaborski M, Slusarski L, Elastomer, 4, 258 (2002)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2007; 31(5): 379-384

    Published online Sep 25, 2007

  • Received on Jan 30, 2007
  • Accepted on May 16, 2007