  • Rheological, Mechanical and Morphological Properties of Poly(acrylonitrile-butadiene-styrene)/Polycarbonate Blends with ABS-g-MAH
  • Song KH, Hong JH, Sung YT, Kim YH, Han MS, Yoon HG, Kim WN
  • ABS-g-MAH를 포함한 Poly(acrylonitrile-butadiene-styrene)과 Polycarbonate 고분자 블렌드의 유변학적, 기계적, 형태학적 물성
  • 송기헌, 홍존희, 승유택, 김연희, 한미선, 윤호규, 김우년
Abstract
Polymer blends containing poly(acrylonitrile-butadiene-styrene)(ABS) and polycarbonate (PC)(70/30, wt%) with compatibilizer were prepared using twin screw extruder. Compatibilizers were prepared by reactive extrusion with the ABS, maleic anhydride(MAH) and dicumyl peroxide(DCP) using twin screw extruder. In the ABS/PC (70/30) blends, tensile strength did not change significantly, but increased from 52.25 to 55.03 MPa when the ABS-g-MAH was added in the amount of 5 phr. From the results of rheological properties, storage modulus of the ABS/PC/ABS-g-MAH blends at low frequencies showed lager value than that of the ABS/PC(70/30) blend. From the results of the morphological properties of the ABS/PC(70/30) blend, it was observed that the drop size of the PC ranged from 1.2 to 1.5 μm and did not change significantly with the addition of the ABS-g-MAH(1~10 phr). From the results of the storage modulus, complex viscosity, and tensile strength of the ABS/PC (70/30) blends, it is found that the ABS-g-MAH is an effective compatibilizer in the ABS/PC (70/30) blends when the ABS-g-MAH is added in the amount of 5 phr.

Poly(acrylonitrile-butadiene-styrene)(ABS)/polycarbonate(PC)(70/30, wt%) 블렌드에 상용화제를 첨가하여 이축 압출기로 시편을 제조하였다. 사용된 상용화제는 ABS에 maleic anhydride(MAH)와 dicumyl peroxide(DCP)를 첨가하여 반응압출을 통하여 그래프트시킨 ABS-g-MAH이었다. ABS/PC(70/30) 블렌드에 상용화제를 5 phr 첨가한 경우 인장강도는 큰 증가는 관찰되지 않았으나, 약 52.25 MPa에서 55.03 MPa로 약간 증가하였다. ABS/PC(70/30) 블렌드의 유변학적 물성을 측정한 결과 상용화제 첨가 시 낮은 진동수 영역에서 탄성률의 증가가 관찰되었으며, 이와 같은 탄성률 증가는 손실탄성률보다 저장탄성률에서 더 잘 나타났다. 또한 ABS/ PC(70/30) 블렌드에 ABS-g-MAH를 1∼10 phr 첨가 시 분산상인 PC의 크기는 약 1.2에서 1.5 m로 큰 변화가 없음을 알 수 있었다. 이상의 연구 결과로서 저장탄성률 증가 및 복소점도 상승 그리고 인장강도의 증가로부터 ABS-g-MAH의 양이 5 phr일 때 ABS/PC(70/30) 블렌드에서 효과적인 상용화제로 작용함을 알 수 있었다.

Keywords: ABS/PC blend; ABS-g-MAH; reactive extrusion; morphology; rheology

References
  • 1. Paul DR, Barlow JW, J. Macromol. Sci.-Rev. Macromol. Chem. Phys., 18, 109 (1980)
  •  
  • 2. Kim WN, Burns CM, Polym. Eng. Sci., 28, 1115 (1988)
  •  
  • 3. Utracki LA, Polymer Blends and Alloys: Thermo- dymnics and RheologyHanser, Munich (1989)
  •  
  • 4. Jin DW, Shon KH, Jeong HM, Polym.(Korea), 20(5), 775 (1996)
  •  
  • 5. Cho CG, Park TH, Kim YS, Polymer, 38(18), 4687 (1997)
  •  
  • 6. Wildes GS, Harada T, Keskkula H, Paul DR, Janarthanan V, Padwa AR, Polymer, 40(11), 3069 (1999)
  •  
  • 7. Wildes G, Keskkula H, Paul DR, Polymer, 40(25), 7089 (1999)
  •  
  • 8. Inberg JPF, Gaymans RJ, Polymer, 43(8), 2425 (2002)
  •  
  • 9. Inberg JPF, Takens A, Gaymans RJ, Polymer, 43(9), 2795 (2002)
  •  
  • 10. Dobrescu V, Cobzaru V, Polym. Symp., 64, 27 (1978)
  •  
  • 11. Lee CH, Lee SG, Kang S, Yung S, Kim JH, Choe S, Polym.(Korea), 23(1), 98 (1999)
  •  
  • 12. Balakrishnan S, Neelakantan NR, Saheb DN, Jog JP, Polymer, 39(23), 5765 (1998)
  •  
  • 13. Qi RR, Qian JL, Zhou CX, J. Appl. Polym. Sci., 90(5), 1249 (2003)
  •  
  • 14. Qi RR, Qian JL, Chen ZF, Jin X, Zhou CX, J. Appl. Polym. Sci., 91(5), 2834 (2004)
  •  
  • 15. Park S, Choe S, Macromol. Res., 13(4), 297 (2005)
  •  
  • 16. Park JH, Kim WN, Kye H, Lee SS, Park M, Kim J, Lim S, Macromol. Res., 13(5), 367 (2005)
  •  
  • 17. Elmaghor F, Zhang LY, Fan R, Li HQ, Polymer, 45(19), 6719 (2004)
  •  
  • 18. Park JH, Sung YT, Kim WN, Hong JH, Hong BK, Yoo TW, Yoon HG, Polym.(Korea), 29(1), 19 (2005)
  •  
  • 19. Jeon BH, Yoon H, Hwang SS, Kim J, Hong SM, Polym.(Korea), 29(2), 127 (2005)
  •  
  • 20. Kim LW, Yoo SH, Kim CK, Polym.(Korea), 31(1), 8 (2007)
  •  
  • 21. Herrera D, Zamora JC, Bello A, Grimau M, Laredo E, Muller AJ, Lodge TP, Macromolecules, 38(12), 5109 (2005)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2007; 31(4): 283-288

    Published online Jul 25, 2007

  • Received on Dec 22, 2006
  • Accepted on Jun 20, 2007