  • Pyrolysis of Teflon
  • Kim YG, Rhee SW
  • Teflon의 열분해에 관한 연구
  • 김영걸, 이시우
Abstract
Major products obtained from pyrolysis of Teflon are C2F4, C3F6 and cyclo-C4F8 and mole percent distribution of each component varied with temperature, pressure and flow rate of inert carrier gas. Experiments were performed under five temperatures between 550 and 800℃ and seven pressures between 760 and 2mmHg. Experiments were also performed under same five temperatures and four flow rates of nitrogen carrier gas between 50 and 170 ml/min. Accumulation of C2F4 was facilitated by reducing the pressure or increasing the flow rate of nitrogen carrier gas. Raising the pyrolysis temperature facilitated C2F4 formation but diminished C2F4 formation. Cyclo-C4F8 was unstable at high temperatures and its amount sharply decreased at high temperatures. It was confirmed from the experimental results that pyrolysis of teflon occurred via formation of C2F4, which was further pyrolyzed to produce C3F6 and Cyclo-C4F8.

Teflon의 열분해에서 주요생성물로 C2F4, C3F6 및 cyclic-C4F8를 얻었으며 열분해 조건에 대한 이들 생산물 분포의 변화를 알아 보았다. Carrier gas를 사용한 실험은 550∼800℃의 온도범위에서 질소의 유량을 50∼170ml/min로 변화시켜가며 하였으며 유량이 증가함에 따라 C2F4가 증가함을 알았다. 같은 온도범위내에서 압력을 대기압에서 진공까지 변화시켜가며 실험하여 압력이 낮아질수록 C2F4가 증가하고 C3F6, cyclic-C4F8가 감소함을 알았다. 모든 경우에 온도가 높아질수록 C2F4의 양은 감소하고 C3F6의 양은 증가하였다. Cylclic-C4F8는 고온에서 불안정하여 분해되므로 그 양이 급격히 감소한다. 실험결과로부터 Teflon의 열분해 mechanism은 고분자사슬에서 C2F4가 떨어져 나오며 그것이 다시 열분해하여 다른 생산물이 생긴다는 가정이 타당함을 알았다.

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1980; 4(1): 40-46

    Published online Jan 25, 1980