  • Preparation and Release Characterization of Biodegradable Poly(ε-caprolactone) Microcapsules Containing Tocopherol
  • Park SJ, Kim KS, Min BG, Hong SK
  • 토코페롤을 함유하는 생분해성 폴리(ε-카프로락톤) 마이크로캡슐의 제조 및 방출 특성
  • 박수진, 김기석, 민병각, 홍성권
Abstract
The biodegradable poly(ε-caprolactone) (PCL) microcapsules containing tocopherol were prepared by oil-in-water emulsion solvent evaporation method. The features of the microcapsules were investigated in the manufacturing conditions and degradation behaviors. The form and structural feature of the microcapsules were measured by scanning electron microscope and X-ray diffraction, respectively. The surface free energy of the microcapsules was executed using contact angle measurement. As a result, the microcapsules were more stable and spherical with poly(vinyl alcohol) given in a surfactant. The surface free energy and crystallinity of microcapsules were decreased with increasing the core concentration, and degradation of PCL was occurred after 21 days. The release behaviors were examined by UV/vis. spectrophotometer. It was found that the release rate of the microcapsules was increased with increasing the stirring rate, due to the increased interface between microcapsules and release media.

토코페롤을 함유하는 폴리(ε-카프로락톤)(PCL) 마이크로캡슐은 액중건조법에 의하여 제조하였고, 제조 조건에 따른 마이크로캡슐의 특성과 PCL 필름을 사용하여 PCL의 분해거동을 측정하였다. 제조된 마이크로캡슐의 크기 및 형태와 구조적 특성은 각각 SEM과 XRD를 이용하여 관찰하였다. 또한, 접촉각 측정을 통하여 심물질의 농도에 따른 마이크로캡슐의 표면자유에너지를 측정하였다. 실험결과, 마이크로캡슐은 유화제로 폴리(비닐 알코올)을 사용한 경우 안정된 구형의 마이크로캡슐이 형성되었고, 마이크로캡슐의 표면자유에너지와 PCL의 결정성은 감소하고, PCL 필름은 약 21일 후 분해가 시작되었다. 토코페롤의 방출특성은 UV/vis.에 의하여 측정하였으며, 마이크로캡슐의 방출속도는 교반속도의 증가와 함께 증가하였다. 이는 교반속도의 증가와 함께 감소된 마이크로캡슐 입자 크기에 의한 방출용액과 마이크로캡슐 사이의 계면의 증가에 의한 것으로 판단된다.

Keywords: microcapsule; poly(ε-caprolactone); tocopherol; surface free energy; release behaviors

References
  • 1. Sosnowski S, Gadzinowski M, Slomkowski S, Macromolecules, 29(13), 4556 (1996)
  •  
  • 2. Mehta RC, Thanoo BC, Deluca PP, J. Control. Release, 41, 277 (1996)
  •  
  • 3. Stenekes RJH, Franssen O, vanBommel EMG, Crommelin DJA, Hennink WE, Int. J. Pharm., 183, 29 (1999)
  •  
  • 4. Jeong SY, Choi JH, Ma YD, Polym.(Korea), 26(4), 523 (2002)
  •  
  • 5. Benita SMicroencapsulation-Methods and Industrial Applications, Marcel Dekker, New York (1996)
  •  
  • 6. Kondo AMicrocapsules Processing and Technology, Marcel Dekker, New York (1979)
  •  
  • 7. Jhonson KA, Adv. Drug Deliv. Rev., 26, 3 (1997)
  •  
  • 8. Oner L, Groves MJ, Pharm. Res., 10, 1385 (1993)
  •  
  • 9. Morita T, Horikiri Y, Suzuki T, Yoshino H, Int. J. Pharm., 219, 127 (2001)
  •  
  • 10. O'Donnell B, McGinity JW, Adv. Drug Del. Rev., 28, 25 (1997)
  •  
  • 11. Takada S, Yamagata Y, Misaki M, Taira K, Kurokawa T, J. Control. Release, 88, 229 (2003)
  •  
  • 12. Park SJ, Yang YJ, Lee JR, Lee HB, Polym.(Korea), 15, 327 (2002)
  •  
  • 13. Kidchob T, Kimura S, Imanishi Y, J. Appl. Polym. Sci., 63(4), 453 (1997)
  •  
  • 14. Sun G, Zhang Z, Int. J. Pharm., 242, 307 (2002)
  •  
  • 15. Kidchob T, Kimura S, Imanishi Y, J. Control. Release, 54, 283 (1998)
  •  
  • 16. Park SJ, Shin YS, Lee JR, J. Colloid Interface Sci., 241(2), 502 (2001)
  •  
  • 17. Hirech K, Payan S, Carnelle G, Brujes L, Legrand J, Powder Technol., 130, 324 (2000)
  •  
  • 18. Shi XY, Tan TW, Biomaterials, 23, 4469 (2002)
  •  
  • 19. Adamson AWPhysical Chemistry of Surface, 5 ed., Chap. 10, John Wiley, New York (1990)
  •  
  • 20. Park SJ, Kim SH, Lee JR, Lee HB, Hong SK, Polym.(Korea), 26(3), 326 (2002)
  •  
  • 21. Ching LS, Mohamed S, J. Agric. Food. Chem., 49, 3101 (2001)
  •  
  • 22. Scalia A, Renda A, Ruberto G, Bonina F, Menegatti E, J. Pharm. Biomed. Anal., 13, 273 (1995)
  •  
  • 23. Yilmaz G, Johnboom ROJ, Feil H, Hennink WE, Carbohydrate Polym., 45, 404 (2001)
  •  
  • 24. Dai L, Li W, Hou X, Colloids Surf. A: Physicochem. Eng. Asp., 125, 27 (1997)
  •  
  • 25. Jr MJ, Davolos MR, Santos FJ, Andrade SJ, J. Non-Cryst. Solids, 247, 98 (1999)
  •  
  • 26. vander Leaden MC, Frens G, Adv. Eng. Mater., 4, 280 (2002)
  •  
  • 27. Wu SPolymer Interface and Adhesion, Marcel Dekker, New York (1982)
  •  
  • 28. Park SJ, Jin JS, J. Colloid Interface Sci., 236(1), 155 (2001)
  •  
  • 29. Garreau SML, Vert M, J. Mater. Sci. Mater. Med., 1, 123 (1990)
  •  
  • 30. Garreau SML, Vert M, J. Mater. Sci. Mater. Med., 1, 131 (1990)
  •  
  • 31. Bachtsi A, Kiparissides C, J. Control. Release, 38, 49 (1996)
  •  
  • 32. Hunter JRFoundation of Colloid Science, Charendon, Oxford (1987)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2004; 28(2): 103-110

    Published online Mar 25, 2004

  • Received on Oct 4, 2003
  • Accepted on Jan 26, 2004