  • Effect of Organic Modifiers and Mixing Times on the Properties of Unsaturated Polyester/Montmorillonite Nanocomposite
  • Kim HG, Lee DH, Seo KH, Kim WS, Park SY, Min KE
  • 유기 개질제의 종류와 혼합 시간에 따른 불포화 폴리에스터/몬모릴로나이트 나노복합체의 제조 및 특성
  • 김호겸, 이동호, 서관호, 김우식, 박수영, 민경은
Abstract
Unsaturated polyester (UP) nanocomposite with montmorillonite (MMT) which contains different types of organic modifiers for nano-filler have been prepared to investigate the effect of chemical structure of organic modifiers and mixing time of all components on properties of products. It was found that the morphology and various physical properties of UP/MMT nanocomposites were influenced by properties of organic modifiers of MMTs. It was also confirmed that the content of MMT does not significantly affect properties of UP/MMT nanocomposites.

서로 다른 종류의 유기 개질제가 층간에 삽입된 세 종류의 몬모릴로나이트 (MMT)를 사용하여 불포화 폴리에스터 (UP)/MMT 나노복합체를 제조하고 유기 개질제의 화학적 구조와 각 성분들의 최종 혼합시간이 최종 나노복합체의 형태구조와 각종 물리적 특성에 미치는 영향을 조사하였다. 최종 혼합 시간은 MMT의 종류에 관계없이 나노복합체의 형태구조와 각종 물성에 별다른 영향을 미치지 못하는 것으로 확인되었으며, MMT의 유기 개질제에 두 개의 수산화기가 포함된 Cloisite 30B의 경우에는 나머지 두 종류의 MMT에 비해 형태구조나 고무 평탄 영역에서의 전단 모듈러스 및 굴곡강도 등은 우수한 것으로 나타났다. 하지만 인장 강도나 열분해 거동, 유리 전이 온도 등은 별다른 차이를 보이지 않았으며, 또한 MMT의 함량에 따른 각종 특성의 선형적인 증가도 관찰되지 않았다.

Keywords: unsaturated polyester; nanocomposite; montmorillonite; organic modifiers; viscoelastic properties

References
  • 1. Messersmith PB, Stupp SJ, J. Mater. Res., 7, 2599 (1992)
  •  
  • 2. Okada A, Usuki A, Mater. Sci. Eng., C3, 109 (1995)
  •  
  • 3. Lee CR, Ihn KJ, Gong MS, Polym.(Korea), 27(4), 392 (2003)
  •  
  • 4. Kang JH, Lyu SG, Choi HK, Sur GS, Polym.(Korea), 25(3), 414 (2001)
  •  
  • 5. Ko MB, Kim J, Choe CR, Korea Polym. J., 8(3), 120 (2000)
  •  
  • 6. Giannelis EP, Adv. Mater., 8, 29 (1996)
  •  
  • 7. Worthy W, Chem. Eng. News, 7, 25 (1987)
  •  
  • 8. Lan T, Pinnavaia TJ, Chem. Mater., 6, 2216 (1994)
  •  
  • 9. Massuam T, Pinnavaia TJ, Mater. Res. Soc. Symp. Proc., 520, 223 (1998)
  •  
  • 10. Vaidya UR, Nadkarni VM, Ind. Eng. Chem. Res., 26, 194 (1987)
  •  
  • 11. Nam JD, Ahn K, Polym. Sci. Technol., 6(5), 459 (1995)
  •  
  • 12. Ferry JDViscoelastic Properties of Polymers, John Wiley & Sons, Inc., 3rd ed., p. 519-537 (1980)
  •  
  • 13. Kornmann X, Lindberg H, Berglund LA, Polymer, 42(4), 1303 (2001)
  •  
  • 14. Vaia RA, Jandt KD, Kramer EJ, Giannelis EP, Macromolecules, 28(24), 8080 (1995)
  •  
  • 15. Hackett E, Manias E, Giannelis EP, J. Chem. Phys., 108(17), 7410 (1998)
  •  
  • 16. Ko MB, Polym. Bull., 45(2), 183 (2000)
  •  
  • 17. Bharadwaj RK, Mehrabi AR, Hamilton C, Trujillo C, Murga M, Fan R, Chavira A, Thompson AK, Polymer, 43(13), 3699 (2002)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2003; 27(6): 589-595

    Published online Nov 25, 2003

  • Received on Jun 20, 2003
  • Accepted on Oct 28, 2003