In this study, the fracture behavior by low velocity impact damage and the tendencies of impact energy absorption were investigated. Low velocity impact tests were performed using a mini tower drop weight impact tester, and graphite powder, carbon black and milled carbon fiber were chosen as additives. Addition of graphite powder increased the maximum load and maintained the stress long until the total penetration happened. At the content of 9 vol%, they showed the maximum of 42% improvement in impact strength compared composites containing no additives. At the test with low impact energy of 0.4 J, impact energy was consumed by delamination in the composite containing no additives, however, as graphite contents increased, the tendency of failure changed to the penetration of the specimen.

저밀도 2-D 탄소/탄소 복합재료의 저속 충격에 의한 파괴 거동과 첨가제에 따른 충격 에너지 흡수 경향을 연구하였다. 저속 충격시험은 mini tower 낙추 충격 시험기를 이용하였으며, 흑연, 카본블랙, 분쇄탄소섬유를 첨가제로 선택하였다. 흑연의 첨가는 최대하중값을 증가시켰으며, 전체적인 관통이 일어나기까지 응력을 오랫동안 유지시키는 효과를 나타내었다. 특히 9 vol%의 함량에서 흑연이 첨가되지 않은 시편보다 약 42%의 충격 흡수 개선을 보였다. 약 0.4 J의 낮은 충격에너지에 의한 충격 회수에 따른 실험에서 첨가제가 첨가되지 않은 시편의 경우, 충격에너지는 층간분리에 의해 소모되고, 흑연의 함량이 증가함에 따라 파괴 경향은 시편의 관통으로 변화함을 관찰할 수 있었다.

Keywords: carbon/carbon composites; low velocity Impact test; impact energy; delamination; penetration