The suspension polymerization of styrene using benzoyl peroxide(BPO) as initiator and poly (vinyl alcohol) (PVA) as suspension stabilizer was carried out in a four-neck flask at 80,85, and 90℃. The particle sizes of the polystyrene beads produced in this study ranged between 0.03 and 0.4cm. The average bead diameter decreased with PVA concentration and water-to-monomer phase ratio, and increased with BPO concentration. The average molecular weight decreased slightly with particle size in a same sample, showing the existence of mass-transfer intrusion. The dispersity ratio varied from 1.6 to 2.3. The Gel Permeation Chromatograms of the polystyrene partices of different sizes have nearly the same shape except for a slight difference in the position of peak occurrence. By measureing the weight of polystyrene formed and calculating the conversion rate of styrene into polystyrene, the overall activation energy of 21600 cal/g·mole was obtained.

Benzoyl peroxide를 개시제로, poly(vinyl alcohol)을 서스펜션안정제로 사용하여 80,85,90℃에서 styrene 단위체를 서스펜션중합하였다. 실험 결과 얻어진 polystyrene 입자의 크기는 그 직경이 0.03~0.4cm의 범위에 있었고 Rosin-Rammler 분포에 기초를 둔 평균입자 크기는 서스펜션 안정제의 농도 및 물과 단위체의 비에 따라 감소했으며 개시제농도에 따라 증가하였다. 같은 batch에서 얻어진 polystyrene의 평균분자량은 입자크기가 커짐에 따라 약간씩 감소했으며, 입자크기에 따른 Gel Permeation Chromatogram은 그 전체적 모양이 거의 같고 다만 정점의 위치가 약간씩 다를 뿐이었다. 반응시간에 따라 생성된 고분자의 량을 각각의 반응온도에 대해 측정하여 그 초기반응속도로부터 21600cal/g·mole의 총괄 활성화에너지를 얻었다.