  • Physical Properties and Flame Retardancy of PU Coatings Polymerized with Two Different Types of Isocyanates and Dichloro-Polyester Polyol
  • Yang IM, Kim SR, Park HJ, Hahm HS, Wu JP, Park HS
  • 두 종류의 이소시아네이트와 디클로로-폴리에스테르 폴리올로부터 중합한 PU 난연도료의 도막물성 및 난연성
  • 양인모, 김성래, 박형진, 함현식, 우종표, 박홍수
Abstract
The dichloro-polyester polyol (DCBAO) which was synthesized in our earlier work was cured at room temperature with two different type of curing agents including Desmodur N-3300 and Desmodur L-75 to get a polyurethane flame-retardant coatings (DCBAO/N-3300=DCBAN and DCBAO/L-75=DCBAL). We could not observe any deterioration of physical properties of the flame-retardant PU coatings (DCBAN and DCBAL) in comparison with the conventional PU coatings. Thermal resistance of DCBAL-type flame-retardant coatings, which was measured by yellowness index difference, was inferior to that of DCBAL-type PU coatings. We believe that this phenomena is attributed to the poor thermal resistance of Desmodur L-75 isocyanate. It was observed that the LOI values were 25∼26% for the PU coatings containing 20∼30 wt% of 2,4-dichlorobenzoic acid.

전보에서 합성한 디클로로-폴리에스테르 폴리올(DCBAO)에 2종류의 이소시아네이트 경화제인 Desmodur N-3300과 Desmodur L-75를 선택하여 상온경화시켜 PU계 난연도료 (DCBAO/N- 3300=DCBAN 및 DCBAO/L-75=DCBAL)를 각각 제조하였다. 제조된 DCBAN과 DCBAL 도료로서 도막물성을 측정한 결과, 양쪽 모두의 도료가 난연처리 후에도 물성저하 현상을 초래하지 않았으며, 별도의 황변성 시험에서 황변성은 DCBAL 쪽이 다소 불량하게 나타나 Desmodur L-75가 황변성과 관련이 있음을 알았다. 또한 난연성분인 2,4-dichlorobenzoic acid의 함량 20∼30 wt%에서 LOI 값 25∼26% 선의 난연효과를 보여주었다.

Keywords: dichloro-polyester polyol; isocyanate; PU flame-retardant coatings; LOI

References
  • 1. Brock T, Groteklaes M, Mischke PEuropean Coatings Handbook, Vincentz Verlag, Hannover, 80 (2000)
  •  
  • 2. Oertel GPolyurethane Handbook, 2nd Ed., Hanser Pub. Co., New York, 55 (1993)
  •  
  • 3. Wicks ZW, Jones FN, Pappas SPOrganic Coatings:Science and Technology, 2nd Ed., Wiley, New York, 180 (1999)
  •  
  • 4. Anderson DG, Vanderberg JT, Anal. Chem., 57, 15 (1985)
  •  
  • 5. Teijin KJpn . Patent 158,273 (1985)
  •  
  • 6. Dainippon Ink & Chem. KK., Jpn. Patent 98,158 (1993)
  •  
  • 7. Park HS, Hahm HS, Park EK, J. Appl. Polym. Sci., 61(3), 421 (1996)
  •  
  • 8. Park HS, Keun JJ, Lee KS, J. Polym. Sci. A: Polym. Chem., 34(8), 1455 (1996)
  •  
  • 9. Park HS, Wu JP, Kim HK, J. Ind. Eng. Chem., 3(4), 282 (1997)
  •  
  • 10. Kim SJ, Park HS, Lee KC, Kim SK, Park EK, J. Ind. Eng. Chem., 3(1), 63 (1997)
  •  
  • 11. Park HS, Ha KJ, Keun JH, Kim TO, J. Appl. Polym. Sci., 70(5), 913 (1998)
  •  
  • 12. Park Hs, Wu JP, Park CH, Kim SK, J. Coat. Technol., 69, 41 (1997)
  •  
  • 13. Dowbenko R, Friedlander C, Gruber G, Prucnal P, Wismer M, Prog. Org. Cocatings., 11, 71 (1983)
  •  
  • 14. Calbo LJHandbook of Coatings Additives, Marcel Dekker, Inc., New York, 1, 511 (1992)
  •  
  • 15. Zisman WA, J. Paint Technol., 44, 42 (1972)
  •  
  • 16. Oldring PKT, Hayward GResins for Surface Coatings, Selective Industrial Training Associates, London, III, 25 (1987)
  •  
  • 17. Nakamichi T, Ishidoya M, J. Coat. Technol., 60, 33 (1988)
  •  
  • 18. Lanson HJEncyclopedia of Polymer Science and Engineering, 2nd Ed., ed by Koroschwitz JI, Wiley, New York, 1, 656 (1985)
  •  
  • 19. Dietliker KKChemistry & Technology of UV & EB Formulation for Coatings, Ink & Paints, Selective Industrial Training Associates, London, 3, 93 (1991)
  •  
  • 20. Kim SJ, Polym. Sci. Technol., 6(2), 118 (1995)
  •  
  • 21. Brock T, Groteklaes, Mischke PEuropean Coatings Handbook, Vincentz Verlag, Hannover, 66 (2000)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2002; 26(2): 193-199

    Published online Mar 25, 2002

  • Received on Sep 19, 2001
  • Accepted on Dec 19, 2001