The crystallization characteristics of metallocene linear low density polyethylene(m-LLDPE)/linear low density polyethylene(LLDPE) blends were investigated. The effect of blending on the induction time for crystallization, spherulites growth rate, and maximum size of spherulites was mainly considered in this study. The formation of separate crystal which is well known crystallization behavior in LLDPE/LDPE blend was not found in m-LLDPE/LLDPE blends. The blending m-LLDPE to LLDPE caused the dramatic decrease in the induction time of m-LLDPE/LLDPE blends but it seems that the blend composition shows less effect on the induction time. Lower branching number in m-LLDPE resulted in the increasing of spherulites growth rate and the maximum size of spherulites is depend upon both the induction time and spherulite growth rate of LLDPE component affected by m-LLDPE.

메탈로센 촉매로 제조된 메탈로센 선형 저밀도 폴리에틸렌(m-LLDPE)과 Ziegler-Natta 촉매에 의하여 제조된 선형 저밀도 폴리에틸렌(LLDPE) 블렌드의 결정화 거동을 고찰하여 보았다. 특히 블렌딩이 이들의 결정화 induction time 및 구정성장 속도 그리고 최대 구정의 크기에 미치는 영향을 중점적으로 살펴보았다. LLDPE/LDPE 블렌드와는 달리 LLDPE에 m-LLDPE를 블렌딩할 경우, 각각의 결정 형성 대신 하나의 결정이 형성됨을 확인하였으며 induction time이 현저히 짧아짐을 알 수 있었다. 하지만 이러한 감소는 블렌드의 조성비에는 크게 영향을 받지 않았다. 또한 블렌딩에 의하여 LLDPE의 구정성장 속도가 증가함을 확인할 수 있었으며, 구정의 최대 크기는 induction time과 구정성장 속도가 LLDPE에 미치는 영향에 따라 달라짐을 알 수 있었다.

Keywords: metallocene low density polyethylene; blends; crystallization; branching number; induction time