  • Effect of Additives on the Orientation of Magnetic Sr-Ferrite Powders in Powder Injection Molded Compacts
  • Cho TS, Jeung WY
  • 분말사출성형체에서 Sr-페라이트 자성분말의 배향도에 미치는 첨가제의 영향
  • 조태식, 정원용
Abstract
The effect of additives on the orientation of magnetic Sr-ferrite powders has been studied during powder injection molding under applied magnetic field for fabricating multi-pole anisotropic sintered Sr-ferrite magnets. The orientation of the Sr-ferrite powders depends sensitively on the fluidity of powder-binder mixture, related to the binder additives and the injection molding temperature, and the magnetic field intensity. The orientation of Sr-ferrite powders is good for the compacts with stearic acid added in the binder system of paraffin wax/carnauba wax/HDPE, but it is poor for the compacts with silane coupling agent added. The orientation of Sr-ferrites higher than 80% is achieved at the following useful conditions; apparent viscosity lower than 2500 poise in 1000 sec(-1) shear rate and applied magnetic field higher than 4 kOe.

다극 이방성 Sr-페라이트 소결자석을 제조하기 위한 자장중 분말사출성형공정에서 Sr-페라이트 자성분말의 배향도에 미치는 결합제의 첨가제 영향이 연구되었다. 외부자기장의 방향에 대한 Sr-페라이트 자성분말의 배향도는 첨가제의 종류, 사출성형온도와 관련한 사출성형체의 유동성과 외부자기장의 세기에 크게 의존하였다. Paraffin wax/carnauba wax/HDPE 3성분계 결합제에 stearic acid를 첨가하면 분말사출성형체의 유동성이 향상되어 Sr-페라이트 자성분말의 배향도가 증가되었으나, silane계 커플링제를 첨가하면 성형체의 유동성이 오히려 감소되어 Sr-페라이트의 배향도가 감소되었다. 80% 이상의 Sr-페라이트 자성분말의 배향도는 사출성형체의 겉보기점도가 2500 poise(1000 sec-1)이하이고 외부자기장의 세기가 4 kOe 이상인 유용한 조건에서 얻어졌다.

Keywords: powder injection molding; orientation of Sr-ferrites; fluidity; stearic acid; coupling agent

References
  • 1. Jeung WY, Cho TS, Moon TJ, J. Korean Magn. Soc., 4, 219 (1994)
  •  
  • 2. Cho TS, Jeung WY, Moon TJ, Polym.(Korea), 19(1), 87 (1995)
  •  
  • 3. Murillo N, Gonzalez J, Guraya C, Gutierrez M, Seco FJ, J. Magn. Magn. Mater., 203, 165 (1999)
  •  
  • 4. German RMPowder Injection Molding, p. 5, MPIF, NJ (1990)
  •  
  • 5. Messler RW, Metal Powder Report, 5, 363 (1990)
  •  
  • 6. Lin ST, German RM, Powder Metall. Intern., 21, 19 (1989)
  •  
  • 7. Wiech REU.S. Patent, 4,305,756 (1981)
  •  
  • 8. Rivers RDU.S. Patent, 4,113,480 (1978)
  •  
  • 9. Denes PA, Ceram. Bull., 41, 509 (1962)
  •  
  • 10. Cullity BDIntroduction to Magnetic Materials, p. 212, Addison-Wesley Publishing Co., Massachusetts (1972)
  •  
  • 11. Chung CI, Rhee BO, Cao MY, Liu CX, Advances Powder Technol., 3, 67 (1986)
  •  
  • 12. Calvert PD, Tormey ES, Pober RL, Ceram. Bull., 65, 669 (1986)
  •  
  • 13. Han CD, Weghe TVD, Shete P, Haw JR, Polym. Eng. Sci., 21, 196 (1981)
  •  
  • 14. Seymour RBAdditives for Plastics, p. 123, Academic Press, NY (1978)
  •  
  • 15. Han CD, Sandford C, Yoo HJ, Polym. Eng. Sci., 18, 849 (1978)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2001; 25(2): 240-245

    Published online Mar 25, 2001

  • Received on Nov 30, 2000