The role of calcium carbonate, glass particulate filler, and discontinuous fibreglass in reinforced unsaturated polyester is experimentally investigated. The composites were manufactured in three forms; particulate filler, fibreglass reinforced and filler-fibre mixed systems. The results indicate that the strength obtained in the composites filled with calcium carbonate was lower than Nielson''s theoretical value. But when the matrix was incorporated with glass particulate filler and coupling agent, the strength was increased higher than that of the theoretical value. The tensile strength of the composites filled with randomly oriented fibreglass showed approximately 35-50% of the Holister''s theoretical strength. And the shear strength decreased with the increase in the length of fibreglass. In mixed system, however, volume fraction of filler which shows the maximum strength was in agreement with optimum volume fraction of composites simply filled with particulate filler.

복합소재로서 탄산칼슘 및 입상 glass 충전재와 fibre glass 단섬유를, polymer matrix로써는 불포화 polyester 수지를 사용하여 입상분산계, 섬유상충전계 그리고 입상일섬유상 혼합계의 삼종의 composites를 성형했다. 그 결과, 입상분산계에서 composites의 강도는 입상 glass의 경우에 용적함유율이 25%이하에서는 Nielsen의 이론값과 거의 일치하였고 그 이상에서는 상회했다. 더우기 coupling agent를 blend했을 때는 매우 좋은 값을 얻었는데 이것은 24-45%에서만 이론값보다 상회하는 탄산칼슘과는 달리 입상 glass와 matrix간의 접착력이 보다 강하다는 것을 보여주는 것이다. 무배향 섬유상 충전계의 인장강도는 Holister의 이론값의 35-50%를 나타냈으며 전단강도는 섬유의 길이에 대략 반비례해서 감소한다는 것을 알 수 있었다. 또한 혼합계에 있어서 강도는 섬유에 크게 의존함을 알았으며 최대강도를 나타내는 입상충전재의 용적함유율이 입상분산계의 최적함유율과 일치함을 알았다.