The polymethylen-bridged dinuclear half-titanocenes[(CH₂)_n(C₅H₄)₂][TiCl₃]₂(n=5(10),7(11),9(12))have been synthesized by treating the distannylated derivatives of the ligands with two equivalents of TiCl₄ in toluene. All complexes are characterized by IR, ¹H NMR, ¹³C NMR and mass spectrometry. In order to examine the catalytic properties of the dinuclear complexes styrene polymerization has been conducted in the presence of MMAO. From the polymerization experiments it was found that (i) all the prepared complexes 10-12 procuced syndiotactic polystyrenes, (ii) the comples 12 holding the longest bridging ligand exhibited the highest activity but produced a polymer having the smallest molecular weight among the polymethylene-bridged dinuclear half-titanocenes. This behavior was attributed to the influence of electron-donating caused by the polymethylene bridge between two active centers as well as the dffdct of steric congestion around metal center caused by the proximal distance between two active sites.

폴리메틸렌 다리를 가진 3가지 dinuclear half-titanocene[(CH₂)_n(C₅H₄)₂][TiCl₃]₂(n=5(10), 7(11), 9(12))을 합성하고 이들의 중합특성을 조사하였다. 이들은 해당되는 리간드의 리튬염을 trimethyltin chloride와 미리 반응시켜 얻은 distannyl기가 치환된 리간드를 TiCl₄와 반응시키는 경로를 통해 합성될 수 있었다. 합성된 화합물들은 IR, ¹H NMR, ¹³C NMR과 질량분석기를 통해 구조와 조성을 규명하였다. 합성된 dinuclear half-titanocene의 중합특성을 조사하기 위해 조촉매 MMAO 존재 하에서 스티렌의 중합실험을 진행하였으며, 그 결과 ( i ) 합성된 세 가지의 촉매는 모두 SPS를 제조하는데 성공적인 촉매였으며, (ii)촉매 중에서는 CpTiCl₃ 사이가 가장 긴 다리리간드로 연결된 화합물 12가 활성면에서는 가장 높았으나 생성된 고분자의 분자량은 가장 낮게 나타났다. 이런 결과들은 다리리간드인 polymethylene이 미치는 전기적 및 입체적 영향으로 설명될 수 있었다. 다리의 길이가 길어지면 polymethylene이 가지는 전자주게 특성이 활성점을 안정화시켜 활성을 향상시키며, 다리의 길이가 길어지면 두 활성점 사이의 거리가 멀어져 활성점 사이에 작용하는 입체적인 영향을 감소시켜 정지반응인 β-H 제거가 잘 일어나 생성되는 syndiotactic polystyrene의 분자량이 감소하게 된다.