  • A study on the Synthesis of ACF/PP-g-AAc Hybrid Fibrous Adsorbent by Irradiation and Their Separation Properties of Heavy Metals
  • Hwang TS, Hwang DS, Park JK
  • 방사선 중합법에 의한 ACF/PP-g-AAc 혼성섬유 흡착제의 합성 및 중금속 분리 특성에 관한 연구
  • 황택성, 황대성, 박정기
Abstract
The ACF/PP-g-AAc copolymers were synthesized by the irradiational grafting of acrylic acid onto ACF/PP fabric. The synthesis of copolymer was evidenced by the bands at 1720, 3600∼3100cm-1 on FT-IR spectrum. After the adsorption of metal ions on ACF/PP-g-AAc copolymers, the morphology with the small deposites on the fiver surface were ovserved by SEM. The optimal time for the metal ion adsorption equilibrium on ACF/PP-g-AAc copolymers was 24 hrs and therir adsorption capacties increased in the order of Mn2+>Cu2+>Co2+>Ni2+. The adsorption capacties of ACF/PP-g-AAC copolymers were invariable after more than 10 times of regeneration.

방사선 전조사법을 이용하여 아크릴산을 ACF/PP 혼성 부직포에 그라프트 반응시켜 ACF/PP-g-AAc 공중합체를 합성하였다. 합성한 공중합체의 FT-IR 결과, 1720, 3600∼3100cm-1부근에서 C=O, -OH에 대한 피크가 확인되었고, 금속이온 흡착후에 공중합체의 표면은 좁쌀알 등과 같은 적은 조직이 관찰되었다. ACF/PP-g-AAc 공중합체의 금속이온에 대한 흡착능의 최적시간은 24시간이었으며 동일 조건하에서의 흡착능은 Mn+2>Cu+2>Co+2>Ni+2의 순서로 Mn+2가 최대흡착능을 나타냈으며 혼합용액에서 금속이온의 흡착에 대한 선택성은 이온반경의 크기에 비례하는 경향을 나타냈었으며, 또한 ACF/PP-g-AAc 공중합체는 10회 이상 흡착능의 변화없이 흡탈착이 가능한 흡착제임을 알 수 있었다.

References
  • 1. Teker M, Saltabas O, Imamoglu M, J. Environ. Sci. Health, A32(8), 2077 (1997)
  •  
  • 2. Shin CS, Lee TH, HWAHAK KONGHAK, 27(4), 588 (1989)
  •  
  • 3. Kim SS, Park M, Hur NH, Choi J, Korean J. Environ. Agric., 10, 11 (1991)
  •  
  • 4. Kostov GK, Turmanova SC, J. Appl. Polym. Sci., 64(8), 1469 (1997)
  •  
  • 5. Kim M, Saito K, Frusaki S, Sugo T, Okamoto J, J. Membr. Sci., 56, 289 (1991)
  •  
  • 6. Lee W, Furusaki S, Saito K, Sugo T, Makuuchi K, Biotechnol. Prog., 12(2), 178 (1996)
  •  
  • 7. Szleifer I, Biophysi. J., 72, 595 (1997)
  •  
  • 8. Furlan L, Defavere VT, Laranjeira MC, Polymer, 37(5), 843 (1996)
  •  
  • 9. Sugo T, Saito K, Membrane, 13, 272 (1988)
  •  
  • 10. Hori T, Saito K, Frusaki S, Sugo T, Okamoto J, Chem. Soc. Jpn., 12, 1792 (1986)
  •  
  • 11. Sugo T, Saito K, Membrane, 71, 58 (1990)
  •  
  • 12. Okamoto J, Sugo T, Katakai A, Omichi H, J. Appl. Polym. Sci., 30, 2967 (1985)
  •  
  • 13. Tsuneda S, Saito K, Frusaki S, J. Membr. Sci., 58, 221 (1991)
  •  
  • 14. Park JS, Nho YC, Hwang TS, Polym.(Korea), 21(4), 701 (1997)
  •  
  • 15. Park JS, Nho YC, Jin JH, Polym.(Korea), 22(1), 39 (1998)
  •  
  • 16. Kwon OH, Nho YC, Yang HS, J. Korean Ind. Eng. Chem., 8(6), 934 (1997)
  •  
  • 17. Trommsdorff E, Kohle H, Lagally P, Markrol. Chem., 1, 169 (1948)
  •  
  • 18. Engelken RD, Mccloud HE, J. Electrochem. Soc., 32, 568 (1985)
  •  
  • 19. Son WG, Moon SM, Baek JH, Kim DC, Park JK, Song HY, Polym.(Korea), 19(4), 433 (1995)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2000; 24(1): 1-7

    Published online Jan 25, 2000