Ultraviolet (UV) absorption properties of poly(ethylene 2,6-naphthalate)(PEN)/poly(ethylene terephthalate)(PET) blend films have been investigated. The effects of blends composition, crystallinity, and transesterification on the UV absorption properties were considered. It has been shown that PEN consisted with a larger aromatic ring (naphthalene) has absorbed UV at higher wavelength than PET. Similar UVabsorption characteristic has been found in PEN/PETblends even if having PEN content as low as 5 wt%. The increase of crystallinity of PEN/PET blends due to the decrease of transesterification caused the increase of UV Cutoff value. However, the UV Cutoff values in PEN and PET films did not affected by the crystallinity of those films.

Poly(ethylene 2,6-naphthalate)/Poly(ethylene terephthalate) (PET) 블렌드 필름에 있어서 블렌드 조성비. 결정화도 그리고 블렌딩시 발현한 상호에스테르 교환반응이 자외선 흡수특성에 미치는 영향을 살펴보았다. 상대적으로 거시적인 aromatic 링인 naphthalene 링을 가지고 있는 PEN은 PET에 비하여 자외선 흡수특성이 우수함을 확인하였다. PEN/PET 블렌드 필름의 경우 5 wt% 정도의 적은 양의 PEN 첨가에 의하여 순수 PEN과 비슷한 자외선 차단특성을 갖음을 알 수 있었다. 순수 PEN과 PET의 경우 필름의 결정화도의 변화는 UV Cutoff 값에 영향을 미치지 못하나 상호에스테르 교환반응 감소에 의한 PEN/PET 블렌드 필름의 결정화도 증가는 UV Cutoff 값을 증가시킴을 알 수 있었다.

Keywords: ultraviolet absorption; poly(ethylene terephthalate); poly(ethylene 2,6-naphthalate); blend; crystallinity; transesterification