Based on the thermodynamic concept, diblock copolymers of polycarbonate and polymethylmethacrylate, PC-b-PMMA, were synthesized and then applied to the polycarbonate blend with SAN to improve the compatibility. Polycarbonate always formed immiscible blend with SAN containing various amount of AN. The average domain size formed by the minor component of blend was varied from 8 μm to 10 μm with AN content of SAN Comparing the average domain size of blend containing PC-b-PMMA block copolymer as compatibilizer with that of blend of polycarbonate and SAN24, the domain size of blend containing compatibilizer was reduced to about 4 μm at the optimum condition. However, the effects of PC-b-PMMA block copolymer on the compatibility of polycarbonate blend with SAN was reduced with increasing polycarbonate content of blend because of thermodynamic limitation related to the interaction energy density between polycarbonate and PMMA.

폴리카보네이트와 acrylonitrile-styrene, SAN, 공중합체 블렌드의 상용성 향상을 위해 열역학적 개념으로 설계된 폴리카보네이트와 폴리메틸메타크릴레이트의 블록 공중합체를, PC-b-PMMA, 제조하고 이의 첨가에 따른 블렌드의 상용성 변화를 조사하였다 상용화제를 첨가하지 않은 폴리카보네이트와 SAN 블렌드는 SAN의 AN 함량과 상관없이 항상 두상의 블렌드를 형성하였으며 분산상의 크기는 SAN내의 AN 함량이 약 24 wt.% 부근에서 최소인 최적의 상용성을 나타내었다. 이때의 수평균 분산상의 크기는 약 8μm였다. 블렌드의 상용화제인 PC-b-PMMA 블록공중합체를 첨가할 경우 분산상의 크기가 최적의 조건하에서 PC/SAN24 블렌드의 분산상 크기의 1/2로 감소하였다. 그러나 블렌드 내의 폴리카보네이트 함량이 증가하면 상용화제의 상호작용 에너지가 0에 가까운 값이기 때문에 분자내의 척력이 작아 PC, PMMA 각 블록의 완전한 상분리가 어렵다는 구조적 특성으로 인해 상용화제의 효과가 감소하였다

Keywords: PC; SAN; block copolymer; domain size; interaction energy density