  • Synthesis and Nonlinear Optical Effects of α-Methylstyrene Copolymers Bearing the Pyridinium and Quinolinium Salt Chromophore
  • Choi DH, Ahn JS, Kim NJ
  • Pyridinium 및 Quinolinium 염기를 포함하는 α-Methylstyrene계 공중합체의 합성 및 비선형 광학 특성에 관한 연구
  • 최동훈, 안종수, 김낙중
Abstract
We synthesized α-methylstyrene copolymers bearing the two different organic salt type chromophores and investigated their second-order nonlinear optical properties using the linear electro-optic (EO) coefficient measurement and second harmonic generation (SHG). In the synthesis of copolymers, N-vinylcarbazole or p-hydroxyphenylmaleimide were employed as a comonomer. In the synthesis of organic salt type chromophore, pyridinium and quinolinium were selected as cationic species and tetraphenylboron was selected as a counterion. In the case of p-hydroxyphenylmaleimide copolymer, we made an attempt to induce thermal crosslinking reaction utilizing diisocyanate. Crosslinking reaction via tetramethylene-m-xylidene diisocyanate was traced by virtue of infrared spectroscopy. The stability of second-order nonlinear optic property was also observed.

두 가지 분자 이온형 발색단을 α-메틸스티렌에 우레탄 기를 연결쇄로 하는 이차비선형 광학 특성 단량체들을 합성하여 이들을 비닐 카바졸 또는 히드록시 말레이미드와 라디칼 중합하여 공중합체를 제조하였다 이 고분자들의 이차 비선형 광학 특성을 일차 전기광학 상수 측정 및 이배 주파수 변조 방법에 의해 그 특성을 조사하고 서로 비교하여 보았다, 이온형 발색단의 양이온 쪽은 피리디니움 또는 퀴놀리니움으로 그리고 음이온 쪽은 테트라페널보론으로 각각 공중합체를 합성하였다. 특히 히드록시 말레이미드 공중합체인 경우, 이관능 이소시아네이트를 이용하여 열적 가교 현상을 in-situ 적외선 분광분석에 의해 규명하였다. 분극 처리 후 이차 비선형 광학 효과의 지속성을 평가하기 위하여 전기광학상수 측정법에 의해 온도를 변화시키면서 효과의 일시 안정성을 조사하였다.

Keywords: nonlinear optics; second harmonic generation; electro-optics; molecular ionic chromophore; corsslink

References
  • 1. Singer KD, Kuzyk MG, Holland WR, Sohn JE, Lalama SJ, Comizzoli RB, Katz HE, Schilling ML, Appl. Phys. Lett., 53, 1800 (1988)
  •  
  • 2. Ye C, Mark TJ, Yang J, Wong GK, Macromolecules, 20, 2322 (1987)
  •  
  • 3. Choi DH, Song S, Lim SJ, Park SY, Kim N, Mol. Cryst. Liq. Cryst., 267(-), 53 (1995)
  •  
  • 4. Yu D, Yu L, Polym. Prepr., 35, 133 (1994)
  •  
  • 5. Pretre P, Kaatz PG, Meier U, Gunter P, Zysset B, Alheim M, Stahelin M, Lehr F, Polym. Prepr., 35, 136 (1994)
  •  
  • 6. Choi DH, Kim HM, Wijekoon WMKP, Prasad PN, Chem. Mater., 4, 1253 (1992)
  •  
  • 7. DeMartino RNU.S. Patent, 4,808,332 (1989)
  •  
  • 8. Park JO, Jang SH, J. Appl. Polym. Sci., 30, 723 (1992)
  •  
  • 9. Marder SR, Perry JW, Schafer WP, Science, 245, 626 (1989)
  •  
  • 10. Nakanishi H, Choi DHin private communication (1995)
  •  
  • 11. Herman WN, Hayden IM, Brower S, Lindsay GA, Stenger-Smith JD, Henry RAOSA & ACS Symp. Ser., p. 18 (1993)
  •  
  • 12. Shi Y, Steier WH, Chen M, Dalton LR, Appl. Phys. Lett., 60, 25 (1992)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1997; 21(1): 125-133

    Published online Jan 25, 1997