  • Study on the Durability of Carbon Fiber/Epoxy Composite by Two Fiber Fragmentation Test
  • Moon CK, Moon SH, SE CS, Cho HH
  • 두 섬유 Fragmentatior 시험법에 의한 탄소섬유/에폭시 복합재료의 내구성에 관한 연구
  • 문창권, 문상현, 서차수, 조현혹
Abstract
Two fiber fragmentation technique was used to investigate the influence of hydrothermal on the interfacial shear strength in the carbon fiber/epoxy system. The uptake of water (wt%) and interfacial shear strength were evaluated up to 60 days of immersion time in distilled water at 75℃ using two fiber fragmentation test specimens of dogbone shape. As a result, it was found that moisture absorption of two fiber doggone specimens increased with time of exposure to hydrothermal. This induced to increase the average critical aspect ratio (Lc/Df) of the fiber fragments. The increase of Lc/Df for hydrothermally treated samples indicated the decrease of the interfacial shear strength by increasing of moisture absorption.

탄소섬유/에폭시 복합재료에서 계면전단강도의 수분에 대한 내구성을 조사하기 위해 두섬유 fragmentation 시험법을 사용하였다. Dogbone형의 두섬유 fragmentation 시험편을 제작하여 75℃의 증류수에 60일까지 침지시켜 수분 흡수량을 측정하였으며, 수분 흡수량에 따른 계면특성 및 계면전단강도를 평가하였다. 그 결과, 침지시간의 경과에 따라 시험편에 흡수된 수분량은 증가하였고, 이러한 수분 흡수량의 증가는 섬유와 수지의 계면을 열화시켜 파단된 섬유길이의 임계 aspect ratio (임계섬유장/섬유직경)를 증가시켰으며, 이것은 곧 수분흡수량의 증가에 의해 복합재료에서 계면전단강도의 감소를 나타내는 것이다.

Keywords: hydrothermal; fragmentation test; interfacial shear strength; durability; degradation

References
  • 1. Bian XS, Ambrosio L, Polym. Compos., 12, 333 (1991)
  •  
  • 2. Lowe GB, Lee TCP, Int. J. Adhes. Adhes., 14, 85 (1994)
  •  
  • 3. Wagner HD, Lustiger A, Composites, 25, 613 (1994)
  •  
  • 4. Gaur U, Miller B, Polym. Compos., 11, 4 (1990)
  •  
  • 5. Miller B, Muri P, Combust. Sci. Technol., 28, 17 (1987)
  •  
  • 6. Gaur U, Miller B, Combust. Sci. Technol., 34, 35 (1989)
  •  
  • 7. Moon CK, J. Appl. Polym. Sci., 44, 561 (1992)
  •  
  • 8. Moon CK, J. Appl. Polym. Sci., 45, 443 (1992)
  •  
  • 9. Moon CK, J. Appl. Polym. Sci., 54(1), 73 (1994)
  •  
  • 10. Takaku A, Arridge RGG, J. Phys. D.: Appl. Phys., 6, 2038 (1973)
  •  
  • 11. Bowling J, Groves GW, J. Mater. Sci., 14, 431 (1979)
  •  
  • 12. Favre J, Merienne MC, Int. J. Adhes. Adhes., 1, 311 (1981)
  •  
  • 13. Penn LS, Lee SM, Fiber Sci. Technol., 17, 91 (1982)
  •  
  • 14. Outwater JO, Murphy MC, Modern Plast., 47, 16 (1970)
  •  
  • 15. Drzal LT, Rich MJ, J. Adhes., 16, 1 (1982)
  •  
  • 16. Drzal LT, SAMPE J., 7 (1983)
  •  
  • 17. Bascom WD, Jensen RM, J. Adhes., 19, 219 (1986)
  •  
  • 18. Curtin WA, J. Mater. Sci., 26, 5239 (1991)
  •  
  • 19. Waterbury MC, Drzal LT, J. Comp. Tech. Res., 13, 22 (1991)
  •  
  • 20. Baxevanakis C, Combust. Sci. Technol., 48, 47 (1993)
  •  
  • 21. Netravali AN, Combust. Sci. Technol., 35, 13 (1989)
  •  
  • 22. Netravali AN, Polym. Compos., 10, 4 (1989)
  •  
  • 23. Mandell JF, Int. J. Adhes. Adhes., 5, 40 (1980)
  •  
  • 24. Moon CK, Mcdonough WG, Polym.(Korea), 19(6), 835 (1995)
  •  
  • 25. Kelly A, Tyson WR, J. Mech. Phys. Solids, 13, 329 (1965)
  •  
  • 26. Miwa M, Osawa T, J. Appl. Polym. Sci., 25, 795 (1980)
  •  
  • 27. Wagner HD, Eitan A, Appl. Phys. Lett., 56, 1965 (1990)
  •  
  • 28. Yavin B, Wagner HD, Polym. Compos., 12, 436 (1991)
  •  
  • 29. Wagner HD, Wood JR, Adv. Compos. Lett., 2, 173 (1993)
  •  
  • 30. Shioya MProceeding of the Adhesion Society, 248 (1994)
  •  
  • 31. Weibull W, J. Appl. Mech., 18, 293 (1951)
  •  
  • 32. Asloun EM, J. Mater. Sci., 24, 3504 (1989)
  •  
  • 33. Schutte CL, Composites, 25, 7 (1994)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1996; 20(1): 116-125

    Published online Jan 25, 1996