  • PAr-g-PS from Polystyrene Macromonomer : Synthesis and Its Use in PBT/PPO Alloy as Compatibilizer
  • Ahn TO, Yim CI, Jeong HM
  • 폴리스티렌 마크로마를 이용한 PAr-g-PS의 합성과 PBT/PPO합금에서 상용화제로의 이용
  • 안태완, 임채익, 정한모
Abstract
Polyarylate (PAr) grafted with polystyrene (PAr-g-PS) was synthesized using dihydroxy-terminated polystyrene (PS) macromonomer of which number average molecular weight was 10,000. Phase separation between the PAr-rich phase and the PS-rich phase in the PAr-g-PS was observed from thermal property measured by differential scanning calorimeter. In the PAr-g-PS/poly(butylene terephthalate) (PBT) binary blend, PAr segment was miscible with PBT and crystallization was hindered by PAr-g-PS. In the PAr-g-PS/poly(2,6-dimethy-1,4-phenylene oxide) (PPO) binary blend PS segment was miscible with PPO. The compatibilizing effect of PAr-g-PS in the PBT/PPO blend was observed in thermal property and morphology.

수평균 분자량이 10,000인 말단에 두개의 히드록시기를 갖는 폴리스티렌(PS) 마크로모노머를 사용하여 PS가 그라프트된 polyarylate (PAr-g-PS)를 합성하고 열적성질을 조사하였다. PAr-s-PS는 PAr 영역의 유리전이온도(Tg)와 PS 영역의 Tg가 분리되어 나타나는 상분리 거동을 보였다. PAr-g-Ps/poly(butylene terephthalate) (PBT) 이원블렌드에서 PAr 세그먼트는 PBT와 상용성을 가졌으며, PAr-g-PS는 PBT의 결정화를 방해하였다. PAr-g-Ps/poly(2,6-di-methyl-1,4-phenylene oxide) (PPO) 이원블렌드에서 PS 세그먼트는 PPO와 상용성을 가졌다. PBT/PPO 블렌드 계에서 PAr-g-PS의 상용화 작용은 열적성질과 모폴로지등으로 부터 관찰할 수 있었다.

Keywords: PS macromonomer; graft copolymer; blend; compatibilizer

References
  • 1. Lausberg D, Muhlbach K, Taubitz C, Angew. Makromol. Chem., 162, 53 (1988)
  •  
  • 2. Wagner M, Wolf BA, Polymer, 34, 1460 (1993)
  •  
  • 3. Peiffer DG, Rabeony M, J. Appl. Polym. Sci., 51, 1283 (1994)
  •  
  • 4. Kobayashi T, Sato M, Takeno N, Mukaida KI, Eur. Polym. J., 29, 1625 (1993)
  •  
  • 5. Tang SC, Hu CP, Ying SK, Polym. J., 22, 70 (1990)
  •  
  • 6. Jo WH, Kim HC, Baik DH, Macromolecules, 24, 2231 (1991)
  •  
  • 7. Auschra C, Stadler R, Voight-Martin IG, Polymer, 34, 2081 (1993)
  •  
  • 8. Ouhadi T, Fayt R, Jerome R, J. Polym. Sci. B: Polym. Phys., 24, 973 (1986)
  •  
  • 9. Tezuka Y, Prog. Polym. Sci., 17, 471 (1992)
  •  
  • 10. Huo PP, Cebe P, Macromolecules, 26, 3127 (1993)
  •  
  • 11. Kimura M, Porter RS, J. Polym. Sci. B: Polym. Phys., 21, 367 (1983)
  •  
  • 12. Bazuin CG, Rancourt L, Villeneuve S, Soldera A, J. Polym. Sci. B: Polym. Phys., 31, 1431 (1993)
  •  
  • 13. Ahn TO, Kim JH, Lee JC, Jeong HM, Park JY, J. Polym. Sci. B: Polym. Phys., 31, 435 (1993)
  •  
  • 14. Ahn TO, Ha YC, Oh MH, Lee SS, Lee SW, Jeong HM, J. Macromol. Sci.-Phys.in press
  •  
  • 15. Peiffer DG, Rabeony M, J. Appl. Polym. Sci., 51(7), 1283 (1994)
  •  
  • 16. Ahn TO, Jeong HM, Lee SM, Lee YJ, Polym.(Korea), 13(4), 309 (1989)
  •  
  • 17. Kim WN, Burns CM, Macromolecules, 20, 1876 (1987)
  •  
  • 18. Ahn TO, Lee S, Jeong HM, Cho K, Angew. Makromol. Chem., 192, 133 (1991)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1995; 19(4): 415-422

    Published online Jul 25, 1995