In this study, unsaturated polyester/silica composites for electric insulation have been prepared. Isophthalate-type unsaturated polyester was compounded with SiO₂ and the compound was cured by peroxide in the presence of cobalt octoate. The effects of Tinuvin P as a UV screener or TiO₂ as a UV absorber on the electrical properties of the composites were investigated. The contents of Tinuvin P and TiO₂ were varied from 0-1.0 wt.% and 0-10 wt.% based on the resin, respectively. The composites were cured at room temperature for 24 hrs and then post-cured at 80 ℃ for 24 hrs. The electrical properties and weather resistance of the composites under the accelerated weathering tests were improved by adding either Tinuvin P or TiO₂; Optimum properties were given when 0.25-0.5 wt.% of Tinuvin P or 2-5 wt.% of TiO₂ was applied. It was concluded that the composites containing either Tinuvin P or TiO₂ could be applied as good insulators.

절연용 불포화 폴리에스테르/실리카 복합재료를 제조하고 제조된 복합재료의 내후성과 전기적 성질간의 상관성을 연구하기 위해 Tinuvin P를 자외선 차단제로, TiO₂를 자외선 홉수제로 사용하여 그 적용량 (Tinuvin P경우는 수지에 대해 0-1.0 wt%, TiO₂의 경우는 수지에 대해 0∼10 wt%)을 변화시키면서 전기적 특성 변화를 조사하였다. 불포화 폴리에스테르 복합재료는 상온에서 24시간 동안 코발트옥테이트 존재하에서 과산화물로 경화시킨 후 80℃에서 24시간 2차 경화시켰다. 강제열화조건하에서 전기적특성과 표면특성 및 몰폴로지를 조사한 결과, 수지에 대해 0.25-0.5%의 Tinuvin P를 사용했을 때와 2-5 wt.%의 TiO₂를 사용했을 때 최적조건인 것으로 나타났으며 그 종류에 관계없이 모두 자외선 안정제가 함유된 복합재료의 절연특성과 내후성이 향상되는 것을 관찰할 수 있었고, 적절한 절연물이라 판단되었다.

Keywords: unsaturated polyester/silica composit; electric insulation; weatherability; TiO₂; Tinuvin P