  • Ultrasonic Velocity in Binary Solution of Polyethylene Oxide With Water
  • Shin WG, Moon TJ, Bae JL, Paik WS
  • Polyethylene oxide/물의 이성분용액에서의 음속
  • 신원규, 문탁진, 배종림, 백운석
Abstract
In this stu요 the sonic velotities of four po1yethylene oxide(PO)/water binary solutions were measured weight of PO, by the method of multireflection of ultrasonic pulses in a few MHz frequency ranges. The sonic velocities and viscosities of the solutons were measured at the temperature ranges of 25℃∼60℃ and at the concentration ranges of 1 wt%∼3 wt% by a pulseecho-overlap method and by an Oswald viscometer, respectively. It is found that the sonic velocities of the solutions increase as the temperatures and the concentrations increase in general

본 실험에서는 분자량이 다른 4개의 polyethylene oxide(PO)물 2성분용액의 음속을 초음파 pulse의 다중반사에 의한 수 MHz의 주파수영역에서 측정하였다. PO/물 2성분용액의 음속과 점성도를 각각 pulse-Echo-Overlap방법과 Oswald점도계를 사용하여 25℃∼60℃의 온도구간과, 1wt%∼3wt%의 농도구간에서 온도와 농도를 각각 변화시키면서 대기압하에서 측정하였다. 용액의 음속은 온도와 농도가 증가함에 따라 증가함을 알 수 있었는데 이는 일반적으로 농도증가에 따른 compressibility의 감소 때문인 것으로 생각된다. 온도와 농도에 따를 점성도는 일반적인 결과를 나타냄을 알수 있었으며, PO의 분자량에 따른 음속의 변화는 분명하게 알 수 있었다.

References
  • 1. Hantington HB, Solid State Phys., 7, 213 (1958)
  •  
  • 2. McSkimin HJ, Andreatch PA, J. Appl. Phys., 35(11), 3312 (1964)
  •  
  • 3. McSkimin HJ, Andreatch PA, J. Appl. Phys., 35(7), 2161 (1964)
  •  
  • 4. Hemphill RB, Rev. Sci. Ins., 39(6), 910 (1968)
  •  
  • 5. Doyle PA, J. Phys. D: Appl. Phys., 13, 163 (1980)
  •  
  • 6. May JE, IRE Nat. Conv. Rec., 6(2), 134 (1958)
  •  
  • 7. Papadakis EP, J. Acoust. Soc. Am., 42, 1045 (1967)
  •  
  • 8. Papadakis EP, J. Acoust. Soc. Am., 47, 806 (1976)
  •  
  • 9. McSkimin HJ, J. Acoust. Soc. Am., 33, 12 (1961)
  •  
  • 10. Forgacs RL, IRE Trans. Inst., 9, 359 (1960)
  •  
  • 11. Hartmann B, Jarzynski J, J. Acoust. Soc. Am., 56, 1469 (1974)
  •  
  • 12. Masuzawa K, Inoue N, Hasegawa T, J. Acoust. Soc. Am., 81, 947 (1987)
  •  
  • 13. Urick KJ, J. Appl. Phys., 18, 983 (1947)
  •  
  • 14. Sivakumar KV, Rajagopal E, Subrahmanyam SV, Acustica, 43, 266 (1979)
  •  
  • 15. Hartmann B, J. Appl. Polym. Sci., 19, 3241 (1975)
  •  
  • 16. Dunbar JI, North AM, Pethrick RA, Steinhauer DB, J. Polym. Sci., 15, 263 (1977)
  •  
  • 17. Heine JC, Snyder WJ, J. Chem. Eng. Data, 29, 175 (1984)
  •  
  • 18. Synder SJ, Synder JR, J. Chem. Eng. Data, 19, 270 (1974)
  •  
  • 19. Gereeze NG, Acustica, 44, 212 (1980)
  •  
  • 20. Spickler P, Ibrahim F, Fast S, Tannenbaum D, Yun S, Stumpf FB, J. Acoust. Soc. Am., 83, 1388 (1988)
  •  
  • 21. Haque MF, Stumpf FB, J. Acoust. Soc. Am., 73, 365 (1983)
  •  
  • 22. Barder M, Cerf R, Acustica, 23, 31 (1970)
  •  
  • 23. Cochran MA, J. Chem. Soc.-Faraday Trans., 70, 215 (1974)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1993; 17(6): 637-643

    Published online Nov 25, 1993