Studies on the Styrenic Polymer 2.Synthesis of Styrene/Acrylonitrile/N-Phenylmaleimide Terpolymer and Properties of Modified ABS
Ahn TO, Kil YS, Park LS
Styrenic Polymer 연구 2. Stryene/ Acrylomitrile/ N- Phenylemaleimide Terpolymer의 합성 및 개질 ABS의 물성
안태완, 길유성, 박이순
Abstract
To enhance the heat resistance of acrylonitrile-butadiene-styrene(ABS), the matrix part(SAN) was modified by introducing N-phellylmaleimide(PMI) monomer, Styrene-acrylonitrile(AN)-PMI terpolymer was synthesized by the semi-continuous emulsion polymerization method with varying PMI content while keeping styrene/AN ratio at 75/25. PSAN terpolymer was blended with g-ABS rubber part utilizing twin screw extrucler to get modified ABS. Modified ABS sample(PSAN : g-ABS= 70 : 30) showed increased thermal stability, hardness, and tensile strength with increasing amount of PMI in the PSAN terpolymer. The impact strength, however, showed maximum at PMI content of 15 wt.% in PSAN. This behavior could be explained by investigating the miscibility of PSAN and shell part of g-ABS(i. e. SAN 25)
ABS수지의 내열성을 증가시키기 위하여 매트릭스인 SAN고분자 주쇄에 고리 구조를 가진 N-phenylmaleimide(PMI) 단량체를 도입하였다. 즉 styrene과 acrylonitrile(AN)의 무게비를 75 : 25로 도정시키고, PMI의 양을 변화시키면서. 삼원 공중합체(PSAN)을 반 연속 유화 중합법으로 합성하였다. 합성된 PSAN은 그라프트 ABS고무(g-ABS)와 용융 블렌드하여 내열성의 향상 및 기계적 성질과의 관계를 조사하였다. 개질 ABS수지(PSAN : g-ABS=70 : 30)의 내열성. 경도 및 인장강도는 PMI의 함량이 증가할수록 증가하였으나 내충격성은 PSAN중 PMI함량이 l5wt%일 때 최대를 나타내었느며 이것을 PSAN 매트릭스와 고무 성분중 SAN 부분과의 상용성 관계를 조사하여 해석하였다.
References
1. Bucknall CBToughened Plastics, p. 90, Applied Science Publishers, Ltd., London (1977)
2. Basdekis CHABS, Van Nostrand Reinold, New York (1964)