  • Polymerization of 2-Propyn-1-ol by Transition Metal Catalysts
  • Gal YS, Jung B, Lee WC, Choi SK
  • 전이금속촉매에 의한 2-프로핀-1-올의 중합
  • 갈영순, 정발, 이원철, 최삼권
Abstract
The polymerization of 2-propyn-1-ol, a propargyl derivative having hydroxy functional group was carried out by various Mo-and W-based catalysts. The catalytic activities of MoCl5-based catalysts were found to be greater than those of WCl6-based catalysts. MoCl5-EtAlCl2 catalyst system gave a quantitative yield of polymer. The polymerization was well proceeded in aromatic and halogenated hydrocarbon solvents such as chlorobenzene, CCl4, 1,1,2-trichloroethylene etc. The polymer yield was increased as the polymerization temperature is increased. Mo(OEt)5 and Mo(OEt)5-EtAlCl2 catalyst systems gave some moderate polymer yields. The infrared spectra of the resulting poly(2-propyn-1-ol) showed neither the acetylenic hydrogen stretching nor the carbon-carbon triple bond stretching frequency. Instead, a new carbon-carbon double bond stretching frequency at about 1650cm-1 appeared, which indicates that the highly conjugated polymer was formed. The resulting poly (2-propyn-1-ol)s were black powder and mostly insoluble in any organic solvents regardless of the catalysts and the polymerization conditions used.

Mo- 및 W-계 촉매를 사용하여 히드록기 관능기가 있는 프로파길유도체인 2-프로핀-1-올의 중합에 대해서 연구하였다. MoCl5계 촉매의 활성이 WCl6계의 그것보다 훨씬 큰 것으로 밝혀졌으며, MoCl5-EtAlCl2 촉매 System의 경우 거의 정량적인 수율을 보였다. 본 중합은 클로로벤젠, 사염화 탄소, 1,1,2-트리클로로에틸렌과 같은 방향족 및 할로겐화 탄화수소용매에서 잘 진행되었으며 중합수율은 중합온도가 증가할수록 철저히 증가하였다. 전이금속알콜사이드인 Mo(OEt)5 및 Mo(OEt)5-EtAlCl2 촉매계를 본 중합에 사용해 본 결과 약 50% 내외의 중합수율을 보여주었다. 합성한 폴리(2-프로핀-1-올)의 적외선분광스펙트럼에서는 아세틸렌의 ≡C-H 및 C≡C 신축띠를 보여주지 않는 대신 1650cm-1 부근에서의 탄소-탄소 이중결합의 특성 피이크가 관찰되었다. 폴리(2-프로핀-1-올)은 사용한 촉매나 조건에 관계없이 유기용매에 녹지 않았으며 대부분 검은색의 분말상이였다.

References
  • 1. Chauser MG, Rodinov YM, Misin VM, Cherkashin MI, Russ. Chem. Rev., 4, 45 (1976)
  •  
  • 2. Katz TJ, Ho TH, Shih NY, Ying YC, Stuat VIW, J. Am. Chem. Soc., 106, 2659 (1984)
  •  
  • 3. Shirakawa H, Louis EJ, MacDiarmid AG, Ching CK, Heeger AJ, J. Chem. Soc.-Chem. Commun., 578 (1987)
  •  
  • 4. Ito T, Shirakawa H, Ikeda S, J. Polym. Sci. A: Polym. Chem., 12, 11 (1974)
  •  
  • 5. Chung TC, MacDiarmid AG, Feldlum F, Heeger AJ, J. Polym. Sci. C: Polym. Lett., 20, 427 (1982)
  •  
  • 6. Pochan JM, Gibson HW, Bailey FC, J. Polym. Sci. C: Polym. Lett., 18, 447 (1980)
  •  
  • 7. Gibson HWHandbook of Conducting Polymers, (ed. by T.A. Skotheim), Chapter 11, Marcel Dekker, Inc., N.Y. (1986)
  •  
  • 8. Masuda T, Higashimura T, Accounts Chem. Res., 17, 51 (1984)
  •  
  • 9. Masuda T, Higashimura T, Adv. Polym. Sci., 81, 121 (1987)
  •  
  • 10. Ho TH, Katz TJ, J. Mol. Catal., 28, 359 (1985)
  •  
  • 11. Wallace KC, William AHL, Davis M, Schrock RR, Organometallics, 8, 644 (1989)
  •  
  • 12. Kminek I, Trekoval J, Makromol. Chem. Rapid Commun., 5, 53 (1984)
  •  
  • 13. Simionescu CI, Percec V, J. Polym. Sci. A: Polym. Chem., 18, 147 (1980)
  •  
  • 14. Percec V, Polym. Prepr., 239 (1983)
  •  
  • 15. Dumitrescu S, Percec V, Simionescu CI, J. Polym. Sci. A: Polym. Chem., 15, 2893 (1977)
  •  
  • 16. Gal YS, Jung B, Choi SK, J. Appl. Polym. Sci., 42, 1793 (1991)
  •  
  • 17. Mort J, Pfister G, Polym. Plast. Tech. Eng., 12, 89 (1979)
  •  
  • 18. Masuda T, Iguchi Y, Tang BZ, Higashimura T, Polymer, 29, 2041 (1988)
  •  
  • 19. Kita H, Sakamoto T, Tanaka K, Okamoto KI, Polym. Bull., 20, 349 (1988)
  •  
  • 20. Hagase Y, Mori S, Matsui K, J. Appl. Polym. Sci., 37, 1259 (1989)
  •  
  • 21. Akopyan LA, Grigoryan SG, Zhamkochyan GA, Matsoyan SG, Vysokomal. Soedin. Ser. A, 17, 2517 (1975)
  •  
  • 22. Akopyan LA, Grigoryan SG, Zhamkochyan GA, Matsoyan SG, Chem. Abstr., 84, 45039v (1976)
  •  
  • 23. Akopyan LA, Ambartsummyan GV, Ovakimyan EV, Matsoyan SG, Vysokomol. Soedin. Ser. A, 19, 271 (1977)
  •  
  • 24. Akopyan LA, Ambartsummyan GV, Ovakimyan EV, Matsoyan SG, Chem. Abstr., 86, 140508 (1978)
  •  
  • 25. Lee WC, Sohn JE, Gal YS, Choi SK, Bull. Korean Chem. Soc., 9, 328 (1988)
  •  
  • 26. Lee WC, Sohn JE, Gal YS, Choi SK, Polym.(Korea), 12(8), 720 (1988)
  •  
  • 27. Lee WC, Huh MW, Gal YS, Choi SK, Polym.(Korea), 13(6), 520 (1989)
  •  
  • 28. Gal YS, Jung B, Lee WC, Choi SK, J. Polym. Sci. A: Polym. Chem.in press, 30 (1992)
  •  
  • 29. Gal YS, Choi SK, Polym.(Korea), 11(6), 563 (1987)
  •  
  • 30. Jang Ms, Kwon SK, Choi SK, Macromolecules, 23, 4135 (1990)
  •  
  • 31. Kim YH, Gal YS, Kim EY, Choi SK, Macromolecules, 21, 1991 (1988)
  •  
  • 32. Cho OK, Kim YH, Choi KY, Choi SK, Macromolecules, 23, 12 (1990)
  •  
  • 33. Furlani A, Russo MV, Carusi P, Licoccia S, Leoni E, Valenti G, Gazz. Chim. Ital., 113, 671 (1983)
  •  
  • 34. Okamura S, Hayashi KJapan 7886 (1963)
  •  
  • 35. Okamura S, Hayashi K, Chem. Abstr., 59, 7671h (1963)
  •  
  • 36. Yoshimura K, Kitade T, Kitamura K, Hozumi K, J. Appl. Polym. Sci., 38, 1011 (1989)
  •  
  • 37. Voronkov MG, Pukhnarevich VB, Sushchinskaya SP, Annenkova VZ, Annenkova VM, Andreeva NJ, J. Polym. Sci. A: Polym. Chem., 18, 43 (1980)
  •  
  • 38. Singleton DM, Eatough DJ, J. Mol. Catal., 8, 175 (1980)
  •  
  • 39. Masuda T, Kawai M, Polymer, 23, 744 (1982)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1992; 16(5): 597-603

    Published online Sep 25, 1992