  • Syntheses and Adsorption Properties for Heavy Metal ions of Chelate Resin Containing Amidoxime Group;2
  • Kim WY, Yug GC, Kim HS, Shin DY
  • 아미드옥심형 킬레이트수지의 합성과 중금속이온 흡착특성: 2
  • 김완영, 육경창, 김형순, 신대윤
Abstract
The chelating resins containing three amidoxime groups per repeating unit of polymer were prepared from chloromethylated AN-STR copolymer beads. The AN-STR copolymers were synthesized by suspension polymerization in the presence of toluene as a diluent. The influences of diluent content and degree of crosslinking on the adsorption capacity of chelating resin for heavy metal ions were examined using with AA or ICP-AES. The chelating resin that was synthesized from AN/STR=1.25(by molar ratio), 7wt% of DVB and 120vol% of toluene showed highest adsoption capacity for Cu(Ⅱ). And the order of adsorption capacity of the chelating resin at optimum pH was Hg(Ⅱ)>Cu(Ⅱ)>UO2(Ⅱ)>Pb(Ⅱ)>Cr(Ⅵ)>Cd(Ⅱ). The adsorption capacity of the chelating resin was greatly affected by co-existing metal ions.

현탁중합으로 가교된 AN-STR의 공중합체를 제조한 다음 클로로메틸화, 시안화, 아미드옥심화하여 중합체의 단위구조당 3개의 아미드옥심기를 배위자로 가지는 킬레이트수지를 제조하고 가교결합체의 양, 희석제의 양과 모노머의 몰비가 중금속이온의 흡착에 미치는 영향을 AA 또는 ICP-AES로 조사하였다. 중금속이온의 흡착을 위한 최적합성조건은 AN/STR의 몰비를 1.25, DVB의 양은 모노머의 7wt%, 희석제는 모노머의 80vol%로 할 때이었으며, 합성된 킬레이트수지의 중금속이온 흡착량은 최대흡착량을 나타내는 pH에서 Hg(II)>Cu(II)>UO2(II)>Pb(II)>Cr(VI)>Cd(II)의 순이었다. 또한 킬레이트수지의 중금속이온 흡착량은 공존이온에 의해 많은 영향을 받았다.

References
  • 1. Dingman J, Siggia S, Barton C, Hiscock KB, Anal. Chem., 44, 1351 (1972)
  •  
  • 2. Collela MB, Siggia S, Barnes RM, Anal. Chem., 52, 967 (1980)
  •  
  • 3. Egawa H, Nakayama M, Nonaka T, Yamamoto H, Uemura K, J. Appl. Polym. Sci., 34, 1557 (1987)
  •  
  • 4. Egawa H, Nakayama T, Nonaka T, Sugihara E, J. Appl. Polym. Sci., 33, 1933 (1987)
  •  
  • 5. Egawa H, Harada H, Nonaka T, J. Chem. Soc. Jpn., 1767 (1980)
  •  
  • 6. Egawa H, Harada H, J. Chem. Soc. Jpn., 959 (1979)
  •  
  • 7. Shouteden FLM, Makromol. Chem., 24, 25 (1957)
  •  
  • 8. Sugasaka K, Katoh S, Taki N, Takahashi A, Umezawa Y, Sep. Sci. Technol., 16, 971 (1981)
  •  
  • 9. Kim WY, Polym.(Korea), 6(5), 347 (1982)
  •  
  • 10. Kim WY, Maeng KS, Polym.(Korea), 6(2), 119 (1982)
  •  
  • 11. Astheimer L, Schenk HJ, Witte EG, Schwochau K, Sep. Sci. Technol., 18, 307 (1983)
  •  
  • 12. Kise H, Sato H, Makromol. Chem., 186, 2449 (1985)
  •  
  • 13. Kun KA, Kunin R, J. Polym. Sci., 6, 2689 (1968)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1992; 16(5): 539-546

    Published online Sep 25, 1992