  • Synthesis & Thermal Properties of Epoxy Resins from Diaminodiphenyl Sulfones 2. Thermal Properties
  • Jung JC, Lee SH, Zin WC
  • 디아미노디페닐 설폰으로부터 에폭시 수지의 합성과 열적성질 2. 열적 성질
  • 정진철, 이상헌, 진왕철
Abstract
In order to compare the thermal properties of the epoxy resins derived from 3,3''-diaminodiphenyl sulfone (3,3''-DDS) and 4,4''-diaminodiphenyl sulfone (4,4''-DDS) , glass transition behaviors of the epoxies from 3,3''-DDS, 4,4''-DDS and 4,4''-diaminodiphenyl methane cured with themselves were measured. The results revealed that the Tg''s depend not only on the chain stiffness but also on the crosslinking density of the cured resins. The cure kinetics measured for 3,3''-DDS epoxy/3,3''-DDS pair by static DSC showed the usually known autoacceleration effect.

3,3''-diaminodiphenyl sulfone(3,3''-DDS) 및 4,4''-diaminodiphenyl sulfone(4,4''-DDS)로 부터 합성된 에폭시 수지의 열적성질을 4,4''-diaminodiphenyl methane(DDM)에서 합성한 에폭시 수지와 상호 비교하기 위하여 이 수지들을 이 세가지 아민으로 경화시켜 Tg를 측정하였다. 그 결과 Tg는 chain stiffness뿐만 아니라 가교밀도에도 영향받음을 알 수 있었다. 3,3''-DDS 에폭시 수지를 3,3''-DDS로 경화시킬 때의 cure kinetics를 조사하니 통상적으로 알려진 autoacceleration 현상을 보였다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1990; 14(6): 597-601

    Published online Dec 25, 1990

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: