A series of novel poly(amide-ester-imide)s were synthesized by polycondensating bifunctional dicarboxylic acids or their acid chlorides. whick contained ester and imide groups within their main chains. with serveral diamines. and then the polymerization conditions were investigated. The monomers and the polymers were characterized by IR spectroscopy, elemental analysis and viscosity measurement. The glass transition temperatures of the polymers were shown in the range of 220∼340℃. and the initial decomposition temperatures were shown in the range of 400∼500℃. And the thermal properties were affected by the positions of amide and ester linkages within polymers''main chains. The polymers were not dissolved in most of common organic solvents, but dissolved in some high polar solvents.

분자내에 에스테르기와 이미드기를 포함하고 있는 새로운 방향족 이염기산 및 이염 기산 클로리드를 합성하고 이들을 방향족 및 지방족 디아민과 중축합시켜 새로운 변성 폴리이미드인 폴리(아미드-에스테르-이미드)를 합성하고 이들의 중합조건에 관하여 검토하였다. 단량체 및 중합체들은 적외선분광분석, 원소분석 및 점도측정에 의해 확인되었다. 중합체들의 유리전이온도는 220∼340℃의 범위, 초기열분해온도는 400∼500℃의 범위에서 나타났으며 이들의 열적성질은 아미드기와 에스테르기의 결합위치에 의해 크게 영향을 받았다. 중합체들은 대개의 유기용매에는 용해되지 않았으나 극성이 강한 일부의 유기용매에는 잘 용해되었다.

Keywords: