Macroporous artificial skins containing antibiotics were prepared by lyophilization of chitosan/PVA blendmer. The tensile strength and elongation under dry state ranged 3.6∼9.4Kg/mm² and 8.7∼ 170%, respectively. These values were increased with the increase of PVA content of the blendmer. The water content was over 80% and the water vapor transmittance rate was about ten times as large as that of the normal skin. The morphological structure of this artificial skin was composed of a dense skin layer and a macroporous inner sponge layer. From the behavior of antimiicrobial releasing and the investigation of the supprression of bacterial proliferation, it was supposed that the artificial skin containing antibiotics could protect the wound surfaces from bacterial invasion to suppress the bacterial proliferation effectively. Animal test results showed that the formation of scar on the wound surface was markedly minimized and the neoepidermal tissue was regenerated well after 20 day of grafting operation.

의료용재료로 응용되는 chitosan과 수용성 합성고분자인 poly(vinyl alcohol)을 블렌드하여 동결건조함으로써 항균제가 함유된 다공성 인공피부를 제조하였다. 기계적인 성질은 건조시 인장강도가 2.6-9.4kg/mm², 신장율은 8.7∼170%의 값을 나타내었으며 PVA의 혼합율이 증가함에 따라 인장강도와 신장율은 증가하였다. 함수율은 80%이상의 높은 함수율을 가지고 있었으며 수분투과도는 정상피부의 약 10배의 값을 나타내었다. Morphology관찰에서 윗부분은 균일막 구조이고 아래는 기공이 연속적으로 존재하는 스폰지 구조를 이루고 있는 것을 관찰할 수 있었다. 항균제의 방출거동 및 세균억제 실험으로부터 함유하고 있는 항균제의 50% 이상이 초기에 방출되는 것을 관찰할 수 있었다. 쥐를 이용한 동물실험 결과 상처부위의 흉터를 최소화할 수 있었으며 조직검사를 통해서 정상피부와 유사한 피부조직이 재생되었음을 관찰할 수 있었다.

Keywords: