Three kinds of polycarbonate glycols were synthesized from the condensation reation of 1,6-hexanediol, 1,4-buthanediol and neopentylglycol with diethycarbonate respectively. And polycarbonate-type polyurethanes were obtained with further reation of these glycols and MDI, and 1,4-buthanediol. Mechanical, thermal properties, water proofness and gas permeability were measured. Glass transition temperature of polyurethane having hexamethylene, tetramethylene group in the main chain appeared near -30℃, -20℃ respectively. However neopentyl type polyurethane has much high T_g around 30-40℃. The mechanical properties of polyurethane increased, but the relative crystallinities decreased with the increasing the amp)tint of chain extender. From the gas permeability test, polycarbonate-type polyurethane membranes having tetramethylene and neopenthyl group showed higher permeability coefficient and higher O₂-selectivity than the polyether or polyester type polyurethane.

1.6-hexanediol, 1,4-butanediol 및 neopentyl glycol을 diethylcarbonate와 각각 축합 반응을 시켜 polycarbonate glycol을 합성하고, 이를 methylenediphenyldiisocyanate(MDI). 1,4-butanediol과 반응시켜 3종의 폴리카보네이트형 우레탄 수지를 합성하였다. 제조한 우레탄 수지의 기계적 성질. 열적 성질 및 내가수분해성 등을 측정하고. 고분자 막 소재로서의 특성을 검토하기 위하여 산소와 질소에 대한 투과실험을 행하였다. 합성한 폴리카보네이트형 우레탄수지 중 hexamethylene계 우레탄 수지는 유리전이온도(T_g)가 -30근 부근의 유연하면서 강인한 필름이 얻어졌으며. tetrame-thyene계 우레탄 수지의 T_g는 -20℃ 부근의 값을 나타냈으나, neopentyl계 우레탄 수지는 T_g가 30∼40℃로 부근의 값을 나타내었다. 쇄연장제의 양을 증가시킴에 따라 기계적 물성은 향상되었으나 상대적 결정화도는 감소되었다. 내가수분해성은 3종 모두 polyether형 우레탄 수지보다 15∼20%가량 우수함을 알 수 있었다. 한편 기체투과 식험 결과 hexamethyle계와 neopentyl계 우레탄 수지는 기존의 우레탄 막 보다 높은 투과계수를 나타냈으며 질소에 대한 산소의 선택성이 크고 온도증가에 따라 투과율이 증가됨을 알 수 있었다.

Keywords: