Polyetherimides(PEI) were synthesized by two different methods and their structure-pro-perty relationship was studied. As for the synthetic methods. nitrodisplacement polymerization and thermal imidization via polyamic arid method were used. PEI samples made by nitrodisplacement had intrinsic viscosity values of 0.13∼ 0.43(g/dl) and glass transition temperatures in the range of 191-213℃. Polyimides with trifluoromethyl groups were synthesized by first making polyamic acid intermediates from dianhydrides and diamine monomers cotaining trifluoromethyl groups followed by subsequent thermal imidization of polyamic acid intermediate. The polyimides with fluorine atoms, imide and flexible ether linkages in the same po1ymer had improved thermall stability compared to the polyetherimides.

몇 종류 폴리에테르이미드(PEI)들의 중합방법과 중합체의 구조 및 열적 성질에 대해 조사하였다. 폴리에테르이미드의 중합방법으로는 니트로 치환 반응과 폴리아믹산 중간체를 거쳐 열이미드화시키는 방법을 사용하였다. 니트로 치환 중합에 의해 생성된 PEI들의 고유점도는 0.13∼0.43 (g/dl)의 값을 나타내었으며 유리전이 온도 (Tg)는 191∼213℃의 범위에 분포하였다. 이들은 상품화된 Ultem의 T_g(213℃) 및 고유점도와 유사하였다. 또 불소원자를 포함하는 폴리이미드의 합성은 불소원자를 가진 diamine 단량체와 dianhydride로 부터 폴리아믹산을 만든 후 이를 열이미드화하여 얻었다. 이와 같이 중합체내 불소원자, 이미드고리 및 유연한 에테르 결합을 동시에 가지는 폴리 이미드들은 폴리에테르이미드들 보다 높은 열적 안정성을 나타내었다.

Keywords: