Fracture toughness of brittle polymers has been increased by incorporating an elastomer as a particulate second phase without sacrificing the other mechanical properties. In this study, unsaturated polyester resin has been toughened by incorporating various elastomers such as carboxylic acid terminated butadiene-acrylonitrile (CTBN), vinyl terminated butadiene-acrylonitrile (VTBN), and polyurethane rubber Commercial butadiene-acrylonitrile rubber shows too poor compatibility with unsaturated polyester resin to get a fine particulate (1∼2μm) incorporation. In order to improve the compatibility between the elastomer and unsaturated polyester resin, it has been tried to synthesize the novel polyurethane rubber. The fracture toughness of unsaturated polyester resin was increased by two times incorporating the novel polyurethane rubber made from poly(tetramethylene ether) glycol and toluene 2,4-diisocyanate.

미세한 고무입자(0.1∼2μm)를 매트릭스 내에 균일하게 분포시켜 고분자 재료의 인성을 증가시키는 방법이 널리 쓰이고 있는데 본 논문에서는 불포화 폴리에스테르 수지의 인성을 증가시키기 위하여 CTBN, VTBN, 폴리우레탄 고무를 강인화제로 사용하였다. 고무에 의한 고분자 재료의 강인화에서 주요 요소인 고무 입자의 크기 및 고무-매트릭스 사이의 결합이 불포화 폴리에스테르 수지의 인성에 미치는 영향을 조사하였다. 기존의 부타디엔-아크릴로니트릴 고무는 불포화 폴리에스테르 수지와 상용성이 좋지 않아 평균 고무입자의 크기가 예상 최적치(1∼2μm) 보다 크고 파괴인성을 1.6배 이상 증가시키지 못했다. 불포화 폴리에스테르 수지와의 상용성을 높이기 위해 새로운 폴리우레탄 고무를 합성하여 강인화제로 사용하였다. Poly(tetramethylene ether) glycol과 toluene 2,4-diisocyanate로 부터 합성한 폴리우레탄 고무를 사용하여 불포화 폴리에스테르 수지의 파괴인성을 2배까지 증가시켰다.

Keywords: