The structures and permeation properties of the polysulfone hollow fiber membranes prepared by dry-wet spinning method were investigated. Spinning solution was composed of polysulfone (Udel P-3500), N, N-dimethylacetamide and polyethylene glycol (molecular weight: 600). The aqueous polyethylene glycol solution with the molecular weight of from 1000 to 35000 was used for the permeation test. The effects of the composition of spinning solution, spinning height, spinning temperature and coagulants on the structures and permeation properties of hollow fibers were studied as main factors. Hollow fibers with a single or double finger structures have the MWCO ranged from 12000 to 35000 by changing the preparation conditions. At 3 atm, water fluxes of these membranes were at the range of 1-83×10^-3㎤/min ㎠.

건습식 방사법에 의한 polysulfone 중공사의 제조에 있어 주요 변수인 방사 원액의 조성, 방사 높이, 방사 온도 및 응고액 등을 변화시켜 이에 따른 중공사의 구조 및 투과 특성을 조사하였다. 사용된 방사 용액은 polysulfone (Udel P-3500), N, N-dimethyl acetamide, polyethyleneglycol (분자량: 600)으로 부성되어 있으며, 투과액은 분자량이 1000에서 35000사이의 polyethyleneglycol을 2000ppm수용액으로 만들어 사용하였다 방사 조건에 따라 단일지상 구조에서 이중지상구조의 중공사막을 제조할 수 있었다. 제조된 중공사막은 분획 분자량이 12000에서 35000 범위의 값을 얻었으며, 투수성은 3기압에서 1-83×10^-3㎤/min ㎠의 범위 에 있었다.

Keywords: