  • Miscibility of Poly(methyl methacrylate) and Polystyrene with Polyarylate
  • Ahn TO, Jeong HM, Lee SM, Lee YJ
  • Poly(methyl methacrylate)와 Polystyrene의 Polyarylate와의 상용성에 관한 연구
  • 안태완, 정한모, 이석민, 이용준
Abstract
The miscibility behaviors of poly(methyl methacrylate) (PMMA) and polystyrene (PS) with polyarylate(PAR)were studied by observing the change of glass transition temperature(Tg) in the blends. PMMA/PAR and PS/PAR blends had both a partial miscibility showing two separate Tg''s slightly migrated toward each other. The PMMA contents in PAR-rich phase changed about 10wt.% with the molecular weight of PMMA (Mw of PMMA:50,000-150,000). but the PS contents in PAR-rich phase did not changed so much with the molecular weight of PS(Mw of PS:30,000-300,000). When the composition of PAR in blends was in the range of 70-8Owt.%, the dispersed particles of PMMA-rich and Ps-rich phase had the diameter of about 1μ.

Poly(methyl methacrylate) (PMMA)와 polystyrene(PS)의 polyarylate(PAR)와의 상용성을 구성 고분자의 분자량과 조성을 변화시키면서 유리전이온도(Tg)의 변화로부터 관찰하였다. PMMA/PAR, PS/PAR계 모두 부분적 상용성을 보였으며 PAR-rich상 중에 PMMA가 녹아 들어가는 정도는 PMMA의 분자량이 50,000-150,000 범위에서 약 10wt.% 정도의 큰 변화를 보이는데 반해 PAR-rich 상중에 PS가 녹아 들어가는 정도는 PS 분자량이 30,000-300,000의 범위에서 변화하여도 큰 변화를 보이지 않았다. 또 PAR의 조성이 많은 경우(70-80wt.%)PMMA-rich 상과 PS-rich상은 1μ크기 정도의 입자로 PAR-rich상 중에 분산하고 있음을 주사전자현미경에서 관찰할 수 있었다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1989; 13(4): 309-315

    Published online May 25, 1989

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: