  • Electroconductive Porous Nylon 6 Film
  • Im SS, In HS, Kang EY
  • 전기전도성 다공질 나일론 6 필름
  • 임승순, 임희석, 강은영
Abstract
To improve the volume and surface conductivity of the nylon 6 films, porous nylon 6 film was prepared and then treated with copper sulfide. which is known as the p-type semiconductor. Optimum conditions for the treating of CuXS were studied. As a result, the amount of the copper compound, the reducing agent and the sulfur containing compound should influence on the amount of absorbed copper sulfide. The surface and volume conductivity of the CuXS-treated porous nylon 6 film were found to be higher by order of 1010 and 108, respectively than those of the original nylon 6 film. The morphology of surface and fracture of the CuXS-treated porous nylon 6 films was investigated with scanning electron microscope(SEM). Temperature dependence of conductivity of the CuXS-treated porous nylon 6 film was investigated. The I-V(Current-Voltage) characteristics and time dependence of samples were observed. Electrical conduction mechanism of CuXS-treated porous nylon 6 films was not dependent on matrix polymer but dependent on the CuXS crystal and the conduction is mainly electronic.

나일론 6필름의 부피 및 표면 전도도를 향상시키기 위하여 다공질 나일론 6필름을 제조하여 P형 반도체로 알려진 CuXS로 처리하였다. CuXS로 처리한 다공질 나일론 6필름의 표면 및 부피 전도도는 각각 1010과 108정도 증가함을 알 수 있었다. 또한 CuXS로 처리한 다공질 나일론 6필름의 전도도의 온도의존성, I-V 특성 및 시간의존성을 조사한 결과 전도 기구는 모상인 나일론 6에는 의존하지 않고 CuXS 결정에 의존하며 전도는 주로 전자전도임을 확인하였다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1988; 12(8): 757-763

    Published online Dec 25, 1988

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: