Pyrrole twas polymerized electrochemically using various electrolytes. The morphology of the polypyrrole film surfaces in contact with the solution always shows aggregation of spheres regardless of the electrolyte used. However, the morphology of the surface in contact with the Pt electrode shorts difference depending on the electrolytes used. The electrode side of the polymer formed with sodium lauryl sulfate as the electrolyte is completely flat while that formed with tetra-n-butyl ammonium perchlorate or tetra-n-butyl ammonium tetra fluoroborate as the electrolyte has many pits. Chemical soaking of the polypyrrole in THF or electrochemical reduction of it causes no change in the morphology. Polypyrrole may be imbedded partially in polyvinyl chloride which covered the Pt electrode only in the early stage of polymerization but a prolonged polymerization seems to tear out the polyvinyl chloride film.

여러가지 전해질을 사용하여 폴리피롤을 중합하였다. 용액을 향한 폴리피롤 필름의 표면 morphology는 사용한 전해질에 상관없이 구형들의 집합체로 나타나 다. 그러나 백금 전극면에 접했던 폴리피롤 필름표면의 morphology는 사용한 전극에 따라 크게 다르다. 즉 유기분자쇄에 연결된 음이온을 사용하면 그 표면은 백금 전극면의 음각을 나타내지만 무기음이온을 사용하면 그 표면은 다공성의 표면을 얻게된다. 전기화학적 중합에 의해 얻어진 폴리피롤 필름은 용출하거나 전기적으로 환원했을때 표면 morphology가 전혀 변하지 않는다. 백금 전극에 폴리염화비닐을 입힌 후 피롤을 중합하면 초기에는 폴리피롤이 폴리염화비닐 필름 속에서 자라며 중합시간이 길어지면 폴리염화비닐 필름을 뚫고 계속해서 용액쪽으로 자라난다.

Keywords: